ML06Al U40068 - GB /T 28906-2012

Grade	ML06Al
China ISC	U40068
Corresponding Standard	GB /T 28906-2012 Hot Rolled Wire Rod for Cold Heading
Classification	Carbon Steel
Properties	Forgability

ML06Al Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr ^*	Ni ^*	Cu ^*	Al ^**
Minimum Value	-	-	0.3	-	-	-	-	-	0.02
Maximum Value	0.08	0.1	0.6	0.03	0.03	0.2	0.2	0.2	-

ML06Al Mechanical Properties

Tensile Strength σ_b Mpa	Reduction of Area ψ %
≤460	≥60

Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		Japan	United States	International Organization for Standardization	European Standard
GB	ISC	JIS	ASTM	ISO	EN
ML06Al	U40068	SWRCH6A	1006	C4C	C4C

ML06Al Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!