ML15 U40152 - GB /T 28906-2012

Grade	ML15
China ISC	U40152
Corresponding Standard	GB /T 28906-2012 Hot rolled wire rod for cold heading
Classification	Carbon Steel
Properties	Forgability Weldability

ML15 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr ^*	Ni ^*	Cu ^*
Minimum Value	0.13	0.1	0.3	-	-	-	-	-
Maximum Value	0.18	0.3	0.6	0.03	0.03	0.2	0.2	0.2

ML15 Mechanical Properties

Tensile Strength σ_b Mpa	Reduction of Area ψ %
≤530	≥50

1 Approximate Comparison Table

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

Russia

United Kingdom

ISC

CNS

JIS

ASTM/AISI

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

ML15

U40152

SWRCH15K

1015

G10150

CC15A
(A4Al)

QSt38-3
(C14C)
Cq15
(C15C)

1.0234
-
1.1132

FR15
FB18
FR18

15nc

0/3

2 Approximate Comparison Table

China		Japan	United States	International Organization for Standardization	European Standard
GB	ISC	JIS	ASTM	ISO	EN	Numerical Grade
ML15	U40152	SWRCH15K	1015	CC15K	C15C	1.0234

3 Approximate Comparison Table

China	Japan	South Korea	United States	International Organization for Standardization	Germany	United Kingdom
GB	JIS	KS	ASTM	ISO	DIN EN/DIN	BS EN/BS
ML15	SWRCH15K	SWCH15K	1015	CC15A	QSt38-3	0/3

ML15 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!