ML40Cr A20404 - GB /T 28906-2012

Grade	ML40Cr
China ISC	A20404
Corresponding Standard	GB /T 28906-2012 Hot Rolled Wire Rod for Cold Heading
Classification	Alloy Steel
Properties	Good Forgability

ML40Cr Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni ^*	Cu ^*
Minimum Value	0.38	0.1	0.6	-	-	0.9	-	-
Maximum Value	0.43	0.3	0.9	0.025	0.025	1.2	0.2	0.2

1 Approximate Comparison Table Cold Heading Steel

China		United States		International Organization for Standardization	Germany		France	Russia	United Kingdom
GB	ISC	ASTM/AISI	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ML40Cr	A20404	5140	G51400	41Cr4E (C16)	41Cr4	1.7035	38C4 42C4	40Х	3/2

2 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		Japan	United States	International Organization for Standardization	European Standard
YB	GB	JIS	ASTM	ISO	EN
QML40Cr	ML40Cr	SCr440	5140	41Cr4	41Cr4

ML40Cr Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!