ML20B A70204 - GB /T 28906-2012

Grade	ML20B
China ISC	A70204
Corresponding Standard	GB /T 28906-2012 Hot Rolled Wire Rod for Cold Heading
Classification	Alloy Steel
Properties	Forgability

ML20B Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr ^*	Ni ^*	Cu ^*	B	Al ^**
Minimum Value	0.18	0.1	0.6	-	-	-	-	-	0.0008	0.02
Maximum Value	0.23	0.3	0.9	0.025	0.025	0.2	0.2	0.2	0.0035	-

Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		Japan	United States	International Organization for Standardization	European Standard
GB	ISC	JIS	ASTM/AISI	ISO	EN
ML20B GB/T 6478-2015 GB/T 6478-2001	A70204	SWRCHB 223 JIS G3508-1	10B21 ASTM A29/A29M-12 ASTM A510/A510-13	CE20BG1 ISO 4954-1993	17B2 EN 10263-4-2001

ML20B Corresponding Standards(Same grade name, different standards)