C72700 Cu-9Ni-6Sn - ASTM B740-2009(R2015) - H2ABC

中文版

Grade	C72700
Old Grade
Corresponding Standard	ASTM B740-2009(R2015) Copper-Nickel-Tin Spinodal Alloy Strip
Classification	Copper and Copper Alloys

C72700 Chemical Element Composition Content (%)

Component	Fe	Mn	Ni	Nb	Pb ^*	Zn	Sn	Mg	More
Minimum Value	-	0.05	8.5	-	-	-	5.5	-	Cu:余量
Maximum Value	0.5	0.3	9.5	0.1	0.02	0.5	6.5	0.15	Cu:余量

C72700 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Strip	Solution (TB00)	410~550	0.05% offset 160~230	≥30
Strip	Solution + cold working 1/4 hard (TD01)	500~660	0.05% offset 330~440	≥12
Strip	Solution + cold working 1/2 hard (TD02)	570~740	0.05% offset 390~550	≥6
Strip	Solution + cold working hard (TD04)	670~860	0.05% offset 530~690	≥3
Strip	solution HT and Cold Worked Spring(TD08)	760~970	0.05% offset 660~790	≥2
Strip	solution HT and Cold Worked Special Spring(TD12)	790~1030	0.05% offset 720~860	-
Strip	Spinodally HT(TX00)	690~900	0.05% offset 380~680	≥15
Strip	1/4 Hard+Spinodal HT(TS01)	790~970	0.05% offset 590~770	≥10
Strip	1/2 Hard+Spinodal HT(TS02)	860~1030	0.05% offset 690~850	≥6
Strip	Hard+Spinodal HT(TS04)	930~1100	0.05% offset 790~930	≥4
Strip	Spring+Spinodal HT(TS08)	1000~1230	0.05% offset 860~1030	≥3
Strip	Special Spring+Spinodal HT(TS12)	1030~1240	0.05% offset 900~1100	≥2

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!