2014A A2014ABE A2014ABD - JIS H 4040-2015

Grade	2014A
Other Names
Corresponding Standard	JIS H 4040-2015 Aluminium and Aluminium Alloy Bars and Wires
Classification	Aluminum and Aluminum Alloys

2014A Chemical Element Composition Content (%)

Component	Fe	Si	Mn	Cr	Ni	Cu	Ti	Zn	Mg	Other Individual	Other Total	More
Minimum Value	-	0.5	0.4	-	-	3.9	-	-	0.2	-	-	Al:余量；Zr+Ti≤0.25
Maximum Value	0.5	0.9	1.2	0.1	0.1	5	0.15	0.25	0.8	0.05	0.015	Al:余量；Zr+Ti≤0.25

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

2014A Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Extruded bar (BE); 10 ≤ d ≤ 200	2014A O	Annealing (O)	≤250	≤135	A50mm ≥12
Extruded bar (BE); 10 ≤ d ≤ 200	2014A T4	Solution Heat Treatment + Natural Aging (T4)	≥345	≥240	≥12
Extruded bar (BE); 10 ≤ d ≤ 200	2014A T4510	T4510	≥345	≥240	≥12
Extruded bar (BE); 10 ≤ d ≤ 200	2014A T4511	T4511	≥345	≥240	≥12
Extruded bars (BE); 12.5 ≤ d ≤ 100	2014A T6	Solid Solution Heat Treatment + Artificial Aging (T6)	≥440	≥400	A ≥6
Extruded bars (BE); 12.5 ≤ d ≤ 100	2014A T6510	Solution Heat Treatment + Stress Relief + Artificial Aging (T6510)	≥440	≥400	≥6
Extruded bars (BE); 12.5 ≤ d ≤ 100	2014A T6511	Solution Heat Treatment + Stress Relief + Artificial Aging (T6511)	≥440	≥400	≥6
Extruded bars (BE); 100 < d ≤ 200	2014A T6	Solid Solution Heat Treatment + Artificial Aging (T6)	≥430	≥350	≥6
Extruded bars (BE); 100 < d ≤ 200	2014AT6510	Solution Heat Treatment + Stress Relief + Artificial Aging (T6510)	≥430	≥350	≥6
Extruded bars (BE); 100 < d ≤ 200	2014A T6511	Solution Heat Treatment + Stress Relief + Artificial Aging (T6511)	≥430	≥350	≥6
Cold drawn rod (BD); d≤80	2014A O	Annealing (O)	≤240	≤125	A50mm ≥10
Cold drawn rod (BD); d≤80	2014A H111	Strain-Hardening (H111)	≤240	≤125	≥10
Cold drawn bars (BD); d≤10	2014A H18	Strain-Hardening - Hard (H18)	≥295	-	-
Cold drawn rod (BD); d≤80	2014A T3	T3	≥380	≥290	A50mm ≥6
Cold drawn rod (BD); d≤80	2014A T351	T351	≥380	≥290	≥4
Cold drawn bars (BD); d ≤ 100	2014A T4	Solution Heat Treatment + Natural Aging (T4)	≥380	≥220	≥10
Cold drawn bars (BD); d ≤ 100	2014A T451	Solution heat-treated, stress-relieved by stretching (T451)	≥380	≥220	≥10
Cold-drawn bar (BD); d ≤ 50	2014A T6	Solid Solution Heat Treatment + Artificial Aging (T6)	≥440	≥360	≥8
Cold drawn bars (BD); d ≤ 100	2014A T651	Solid Solution Heat Treatment + Stretching Stress Relief + Artificial Aging (T651)	≥450	≥380	≥8

① A50mm、A（5.65√S0）- gauge length，S0-Specimen area，s=S0，unit mm sq
② d-diameter、thickness or width across flats, unit mm；s - cross section area, unit mm sq

Approximate Comparison Table Wrought Aluminum and Aluminum Alloy

China	Japan	United States		International Organization for Standardization		France	European Standard	United Kingdom
GB	JIS	ASTM	UNS	ISO	Numerical Grade	NF EN/NF	EN	Commercial Grade	BS EN/BS
2014A	2014A A92014	2014A	A92014	AlCu4SiMgMn(A)	A92014	A-U4SG(A) 2014 A92014	EN-AW-AlCu4SiMg(A)	H15	2014A A92014

2014A Corresponding Standards(Same grade name, different standards)

1	GB /T 3190-2008
	2014A
2	GB /T 3190-2020
	2014A
3	JIS H 4040-2015
	2014A A2014ABE A2014ABD
4	GB /T 3191-2019
	2014A
5	GB /T 3880.1-2012
	2014A
6	JIS H 4000-2022
	2014A A2014AP