Grade 2017
Other Names
Corresponding Standard JIS H 4040-2015
Aluminium and aluminium alloy bars and wires
Classification Aluminum and Aluminum Alloys
Properties Strength Machinability
2017 Chemical Element Composition Content (%)
Component Fe Si Mn Cr Cu Ti Zn Mg Other Individual Other Total More
Minimum Value - 0.2 0.4 - 3.5 - - 0.4 - - Al:余量
Maximum Value 0.7 0.8 1 0.1 4.5 0.15 0.25 0.8 0.05 0.15
"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.
2017 Mechanical Properties
condition Mark
Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
%
Extruded bar (BE); all sizes 2017 O Annealing (O) ≤245 ≤125 A50mm
≥16
Extruded Rod (BE); All Sizes; s≤700 2017 T4 Solution Heat Treatment + Natural Aging (T4) ≥345 ≥215 ≥12
Extruded Rod (BE); All Sizes; s≤700 2017 T42 Solution Treatment + Natural Aging (T42) ≥345 ≥215 ≥12
Extruded Rod (BE); All Sizes; 700<s≤1000 2017 T4 Solution Heat Treatment + Natural Aging (T4) ≥335 ≥195 ≥12
Extruded Rod (BE); All Sizes; 700<s≤1000 2017 T42 Solution Treatment + Natural Aging (T42) ≥335 ≥195 ≥16
Drawn Rod (BD), Wire (W); d≤3 2017 O Annealing (O) ≤245 - -
Drawn bar (BD), wire (W); 3<d≤100 2017 O Annealing (O) ≤245 - ≤16
Drawn bar (BD), wire (W); 3<d≤10 2017 H13 Strain-Hardening - 3/8 Hard (H13) 205~275 - -
Drawn Rod (BD), Wire (W); d≤3 2017 T4 Solution Heat Treatment + Natural Aging (T4) ≥380 - -
Drawn bar (BD), wire (W); d≤3; s≤300 2017 T42 Solution heat treatment + natural aging (42) ≥380 - -
Drawn Rod (BD), Wire (W); 3<d≤100; s≤300 2017 T4 Solution Heat Treatment + Natural Aging (T4) ≥380 ≥225 ≥12
Drawn Rod (BD), Wire (W); 3<d≤100; s≤300 2017 T42 Solution heat treatment + natural aging (42) ≥380 ≥225 ≥12
① A50mm、A（5.65√S0）- gauge length，S0-Specimen area，s=S0，unit mm sq
② d-diameter、thickness or width across flats, unit mm；s - cross section area, unit mm sq
1 Approximate Comparison Table Wrought aluminum and aluminum alloy
China Japan United States International Organization for Standardization Germany European Standard
GB JIS ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. EN
2017 2017
A92017 		2017 A92017 AlCu4MgSi A92017 AlCu4Mg1 3.1325
A92017 		EN-AW-AlCu4MgSi
2 Approximate Comparison Table Aluminium and aluminium alloy
Japan United States International Organization for Standardization Germany France European Standard Russia
JIS UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST
2017 A92017 AlCuMgSi AlCuMg1 3.1325 2017A ENAW-AlCu4MgSi(A) ENAW-2017A D1
2017 Corresponding Standards(Same grade name, different standards)
1 JIS H 4040-2006
2017 A2017 W A2017 BD A2017 BE
2 GB /T 3195-2016
2017
3 GB /T 3190-2020
2017
4 JIS H 4040-2015
2017 A2017 W A2017 BD A2017 BE
5 ISO 209-2007
2017 (AlCu4MgSi)
6 GB /T 3191-2019
2017
7 GB /T 3880.1-2012
2017

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!