2017A 2017A BE 2017A BD - JIS H 4040-2015

Grade	2017A
Other Names
Corresponding Standard	JIS H 4040-2015 Aluminium and aluminium alloy bars and wires
Classification	Aluminum and Aluminum Alloys
Properties	Machinability

2017A Chemical Element Composition Content (%)

Component	Fe	Si	Mn	Cr	Cu	Zn	Mg	Other Individual	Other Total	More
Minimum Value	-	0.2	0.4	-	3.5	-	0.4	-	-	Al余量；Zr+Ti≤0.25
Maximum Value	0.7	0.8	1	0.1	4.5	0.25	1	0.05	0.15	Al余量；Zr+Ti≤0.25

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

2017A Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Extruded bar (BE); 10≤d≤100	2017A O	Annealing (O)	≤250	≤150	A ≥10
Extruded bar (BE); 10 ≤ d ≤ 80	2017A T4	Solution Heat Treatment + Natural Aging (T4)	≥390	≥265	≥10
Extruded bar (BE); 80 < d ≤ 200		Solution Heat Treatment + Natural Aging (T4)	≥360	≥220	≥7
Extruded bar (BE); 10 ≤ d ≤ 80	207A T4510	Solution heat treatment + stress relief + natural aging (T4510)	≥390	≥265	≥10
Extruded bar (BE); 80 < d ≤ 200		Solution heat treatment + stress relief + natural aging (T4510)	≥360	≥220	≥7
Extruded bar (BE); 10 ≤ d ≤ 80	2017A T4511	Solution heat treatment + stress relief + natural aging (T4511)	≥390	≥265	≥10
Extruded bar (BE); 80 < d ≤ 200		Solution heat treatment + stress relief + natural aging (T4511)	≥360	≥220	≥7
Cold drawn rod (BD); d≤80	2017A O	Annealing (O)	≤240	≤125	A50mm ≥10
Cold drawn rod (BD); d≤80	2017A H111	Strain-Hardening (H111)	≤240	≤125	≥10
Cold drawn bars (BD); d≤10	2017A H18	Strain-Hardening - Hard (H18)	≥315	-	-
Cold drawn rod (BD); d≤80	2017A T3	Solution heat treatment + cold working hardening + natural aging (T3)	≥400	≥250	≥8
Cold drawn rod (BD); d≤80	2017A T351	Solution heat treatment + cold working hardening + stretching to relieve stress + natural aging (T351)	≥400	≥250	≥6
Cold-drawn bar (BD); d ≤ 50	2017A T4	Solution Heat Treatment + Natural Aging (T4)	≥380	≥220	A ≥10
Cold Drawn Bar (BD); 50<d≤100		Solution Heat Treatment + Natural Aging (T4)	≥390	≥235	≥10
Cold-drawn bar (BD); d ≤ 50	2017A T451	Solution heat-treated, stress-relieved by stretching (T451)	≥380	≥220	≥10
Cold Drawn Bar (BD); 50<d≤100		Solution heat-treated, stress-relieved by stretching (T451)	≥390	≥235	≥10

① A50mm、A（5.65√S0）- gauge length，S0-Specimen area，s=S0，unit mm sq
② d-diameter、thickness or width across flats, unit mm；s - cross section area, unit mm sq

1 Approximate Comparison Table Wrought Aluminum and Aluminum Alloy

China	Japan	United States		International Organization for Standardization		France	European Standard
GB	JIS	ASTM	UNS	ISO	Numerical Grade	NF EN/NF	EN
2017A	2017A A92017	2017A	A92017	AlCu4MgSi(A)	A92017	A-U4GS 2017A A92017	EN-AW-AlCu4MgSi(A)

2 Approximate Comparison Table Wrought Aluminum and Aluminum Alloy

China		Japan	United States		International Organization for Standardization		European Standard
GB	ISC	JIS	ASTM	UNS	ISO	Numerical Grade	EN
2B11 (LY8)	2017A	2017A A92017	2017A	A92017	AlCu4MgSi(A)	A92017	EN-AW-AlCu4MgSi(A)

2017A Corresponding Standards(Same grade name, different standards)

1	GB /T 3190-2008
	2017A
2	DIN 1725-1-1983
	2017A AlCuMg1 3.1325
3	GB /T 3190-2020
	2017A
4	JIS H 4040-2015
	2017A 2017A BE 2017A BD
5	GB /T 3191-2019
	2017A
6	GB /T 3880.1-2012
	2017A

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!