2117 A2117 W - JIS H 4040-2015

Grade	2117
Other Names
Corresponding Standard	JIS H 4040-2015 Aluminium and Aluminium Alloy Bars and Wires
Classification	Aluminum and Aluminum Alloys

2117 Chemical Element Composition Content (%)

Component	Fe	Si	Mn	Cu	Zn	Mg	Other Individual	Other Total	More
Minimum Value	-	-	-	2.2	-	0.2	-	-	Al:Remainder；Zr+Ti≤0.25
Maximum Value	0.7	0.8	0.1	3	0.25	0.5	0.05	0.15	Al:Remainder；Zr+Ti≤0.25

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

2117 Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Cold Drawn Wire (W); 3≤d≤10	2117 H15	Strain - Work hardened - 5/8 hard (H15)	195~245	-	-
Cold-drawn wire (W); d≤18	2117 H18	Strain-Hardening - Hard (H18)	≥260	-	-
Cold Drawn Wire (W); 3≤d≤10	2117 T4	Solution Heat Treatment + Natural Aging (T4)	≥265	≥125	A50mm ≥18

① A50mm、A（5.65√S0）- gauge length，S0-Specimen area，s=S0，unit mm sq
② d-diameter、thickness or width across flats, unit mm；s - cross section area, unit mm sq

Approximate Comparison Table Wrought Aluminum and Aluminum Alloy

China	Japan	United States		International Organization for Standardization		Germany		European Standard
GB	JIS	ASTM	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	EN
2117	2117 A92117	2117	A92117	AlCu2.5Mg	A92117	AlCu2.5Mg0.5	3.1305 A92117	EN-AW-AlCu2.5Mg

2117 Corresponding Standards(Same grade name, different standards)

1	GB /T 3190-2008
	2117
2	JIS H 4040-2006
	2117 A2117 WS A2117 W
3	GB /T 3195-2016
	2117
4	DIN 1725-1-1983
	2117 AlCu2.5Mg0.5 3.1305
5	GB /T 3190-2020
	2117
6	JIS H 4040-2015
	2117 A2117 W

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!