1050A A1050A BE A1050A BD - JIS H 4040-2015

Grade	1050A
Other Names
Corresponding Standard	JIS H 4040-2015 Aluminium and Aluminium Alloy Bars and Wires
Classification	Aluminum and Aluminum Alloys

1050A Chemical Element Composition Content (%)

Component	Fe	Si	Mn	Cu	Ti	Al	Zn	Mg	Other Individual
Minimum Value	-	-	-	-	-	99.5	-	-	-
Maximum Value	0.4	0.25	0.05	0.05	0.05	-	0.07	0.05	0.03

1050A Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Extruded Rod (BD); All Sizes	1050A O	Annealing (O)	60~95	≥20	-
Extruded Rod (BD); All Sizes	1050A H111	Strain-Hardening (H111)	60~95	≥20	A50mm ≥23
Extruded bar (BD); d≤35 (30*)	1050A H112	Strain-Hardening (H112)	≥65	≥20	≥23
Cold drawn bars (BD); d ≤ 30	1050A O	Annealing (O)	≥60	≥20	A ≥25
Cold drawn bars (BD); d ≤ 30	1050A H14	Strain-hardening-1/2 hard (H14)	≥100	≥70	≥6
Cold Drawn Rod (BD); d≤15 (5*)	1050A H16	Strain-hardening-3/4 hard (H16)	120~160	≥105	≥4
Cold drawn bars (BD); d≤10	1050A H18	Strain-Hardening - Hard (H18)	≥130	≥110	≥3

① A50mm、A（5.65√S0）- gauge length，S0-Specimen area，s=S0，unit mm sq
② d-diameter、thickness or width across flats, unit mm；s - cross section area, unit mm sq

Approximate Comparison Table Wrought Aluminum and Aluminum Alloy

China	Japan	United States		International Organization for Standardization		France	European Standard	Russia
GB	JIS	ASTM	UNS	ISO	Numerical Grade	NF EN/NF	EN	GOST
1050A	1050A A91050	1050A	A91050	Al99.5(A)	A91050	A5 1050A A91050	EN-AW-Al99.5(A)	АД0/1011

1050A Corresponding Standards(Same grade name, different standards)

1	GB /T 3190-2008
	1050A
2	GB /T 3190-2020
	1050A
3	JIS H 4040-2015
	1050A A1050A BE A1050A BD
4	GB /T 3191-2019
	1050A (L3)
5	GB /T 3880.1-2012
	1050A
6	JIS H 4000-2022
	1050A A1050AP

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!