2011 A2011 BE A2011 BD - JIS H 4040-2015

Grade	2011
Other Names
Corresponding Standard	JIS H 4040-2015 Aluminium and aluminium alloy bars and wires
Classification	Aluminum and Aluminum Alloys
Properties	Strength Machinability

2011 Chemical Element Composition Content (%)

Component	Fe	Si	Cu	Pb	Zn	Bi	Other Individual	Other Total	More
Minimum Value	-	-	5	0.2	-	0.2	-	-	Al:余量
Maximum Value	0.7	0.4	6	0.6	0.3	0.6	0.05	0.15	Al:余量

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

2011 Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Cold-drawn bar (BD), Wire (W); 3≤d≤38	A2011 T3	Solution treatment + cold working + natural aging (T3)	≥310	≥260	A50mm ≥10
Cold Drawn Bar (BD), Wire (W); 38<d≤50		Solution treatment + cold working + natural aging (T3)	≥295	≥235	≥12
Cold Drawn Bar (BD), Wire (W); 50<d≤80		Solution treatment + cold working + natural aging (T3)	≥280	≥205	≥14
Cold-drawn bar (BD), Wire (W); 3≤d≤80	A2011 T8	Solution treatment + cold working + artificial aging (T8)	≥370	≥270	≥10
Cold drawn bars (BD), wire (W); d≤10	A2011 H18	Strain - Work hardened - hard (H18)	≥240	-	-
Cold-drawn bar (BD), Wire (W); d≤18	A2011 H13	Strain-Hardening - 3/8 Hard (H13)	155~225	-	-
Extruded Rod (BE); 3≤d≤200	A2011 T4	Solution Heat Treatment + Natural Aging (T4)	≥275	≥125	≥16
Extruded Rod (BE); 3≤d≤75	A2011 T6	Solid Solution Heat Treatment + Artificial Aging (T6)	≥310	≥230	≥10
Extruded Bar (BE); 75<d≤160		Solid Solution Heat Treatment + Artificial Aging (T6)	≥295	≥195	≥8

① A50mm、A（5.65√S0）- gauge length，S0-Specimen area，s=S0，unit mm sq
② d-diameter、thickness or width across flats, unit mm；s - cross section area, unit mm sq

Approximate Comparison Table Wrought aluminum and aluminum alloy

China	Japan	United States		International Organization for Standardization		Germany		European Standard
GB	JIS	ASTM	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	EN
2011	2011 A92011	2011	A92011	AlCu6BiPb	A92011	EN-AW-AlCu6BiPb	3.1655 A92011	EN-AW-AlCu6BiPb

2011 Corresponding Standards(Same grade name, different standards)

1	GB /T 3190-2008
	2011
2	JIS H 4040-2006
	2011 A2011 W A2011 BD
3	DIN 1725-1-1983
	2011 AlCuBiPb 3.1655
4	GB /T 3190-2020
	2011
5	JIS H 4040-2015
	2011 A2011 BE A2011 BD A2011 W

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!