Home Material JIS H 4040-2015
简体 | 繁體
Grade 2014
Other Names
Corresponding Standard JIS H 4040-2015
Aluminium and aluminium alloy bars and wires
Classification Aluminum and Aluminum Alloys
2014 Chemical Element Composition Content (%)
Component Fe Si Mn Cr Cu Ti Zn Mg Other Individual Other Total More
Minimum Value - 0.5 0.4 - 3.9 - - 0.2 - - Al余量
Maximum Value 0.7 1.2 1.2 0.1 5 0.15 0.25 0.8 0.05 0.15
"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.
2014 Mechanical Properties
condition Mark
Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
%
Extruded bar (BE); all sizes 2014 O Annealing (O) ≤250 ≤135 A50mm
≥12
Extruded bar (BE); all sizes 2014 T4 Solution Heat Treatment + Natural Aging (T4) ≥345 ≥240 ≥12
Extruded bar (BE); all sizes 2014 T4510 Solution treatment + tensile stress relief + natural aging (T4510) ≥345 ≥240 ≥12
Extruded bar (BE); all sizes 2014 T4511 Solution treatment + tensile stress relief + natural aging (T4511) ≥345 ≥240 ≥12
Extruded bar (BE); all sizes 2014 T42 Solution Treatment + Natural Aging (T42) ≥345 ≥205 ≥12
Extruded bar (BE); d ≤ 12 2014 T6 Solid Solution Heat Treatment + Artificial Aging (T6) ≥410 ≥365 ≥7
Extruded bar (BE); 12 < d ≤ 19 Solid Solution Heat Treatment + Artificial Aging (T6) ≥440 ≥400 ≥7
Extruded bar (BE); d>19, s≤160 Solid Solution Heat Treatment + Artificial Aging (T6) ≥470 ≥410 ≥7
Extruded bar (BE); d>19, 160<s≤200 Solid Solution Heat Treatment + Artificial Aging (T6) ≥470 ≥400 ≥6
Extruded bar (BE); d > 19, 200 < s ≤ 250 Solid Solution Heat Treatment + Artificial Aging (T6) ≥450 ≥380 ≥6
Extruded bar (BE); d > 19, 250 < s ≤ 300 Solid Solution Heat Treatment + Artificial Aging (T6) ≥430 ≥365 ≥6
Extruded bar (BE); d ≤ 12 2014 T6510 Solution Heat Treatment + Stress Relief + Artificial Aging (T6510) ≥410 ≥365 ≥7
Extruded bar (BE); 12 < d ≤ 19 Solution Heat Treatment + Stress Relief + Artificial Aging (T6510) ≥440 ≥400 ≥7
Extruded bar (BE); d>19, s≤160 Solution Heat Treatment + Stress Relief + Artificial Aging (T6510) ≥470 ≥410 ≥7
Extruded bar (BE); d>19, 160<s≤200 Solution Heat Treatment + Stress Relief + Artificial Aging (T6510) ≥470 ≥400 ≥6
Extruded bar (BE); d > 19, 200 < s ≤ 250 Solution Heat Treatment + Stress Relief + Artificial Aging (T6510) ≥450 ≥380 ≥6
Extruded bar (BE); d > 19, 250 < s ≤ 300 Solution Heat Treatment + Stress Relief + Artificial Aging (T6510) ≥430 ≥365 ≥6
Extruded bar (BE); d ≤ 12 2014 T6511 Solution Heat Treatment + Stress Relief + Artificial Aging (T6511) ≥410 ≥365 ≥7
Extruded bar (BE); 12 < d ≤ 19 Solution Heat Treatment + Stress Relief + Artificial Aging (T6511) ≥440 ≥400 ≥7
Extruded bar (BE); d>19, s≤160 Solution Heat Treatment + Stress Relief + Artificial Aging (T6511) ≥470 ≥410 ≥7
Extruded bar (BE); d>19, 160<s≤200 Solution Heat Treatment + Stress Relief + Artificial Aging (T6511) ≥470 ≥400 ≥6
Extruded bar (BE); d > 19, 200 < s ≤ 250 Solution Heat Treatment + Stress Relief + Artificial Aging (T6511) ≥450 ≥380 ≥6
Extruded bar (BE); d > 19, 250 < s ≤ 300 Solution Heat Treatment + Stress Relief + Artificial Aging (T6511) ≥430 ≥365 ≥6
Extruded bar (BE); d≤19 2014 T62 Solution Heat Treatment and Precipitation Heat Treatment (T62) ≥410 ≥365 ≥7
Extruded bar (BE); d>19, s≤160 Solution Heat Treatment and Precipitation Heat Treatment (T62) ≥410 ≥365 ≥7
Extruded bar (BE); d>19, 160<s≤200 Solution Heat Treatment and Precipitation Heat Treatment (T62) ≥410 ≥365 ≥6
Cold Drawn Bar (BD); 3≤d≤100 2014 O Annealing (O) ≤245 ≥12
Cold drawn rod (BD); d≤80 2014 T3 Solution heat treatment + cold working hardening + natural aging (T3) ≥380 ≥290 ≥6
Cold drawn rod (BD); d≤80 2014 T351 Solution heat treatment + cold working hardening + stretching to relieve stress + natural aging (T351) ≥380 ≥290 ≥4
Cold drawn bar (BD); 3≤d≤100, s≤230 2014 T4 Solution Heat Treatment + Natural Aging (T4) ≥380 ≥220 ≥16
Cold drawn bar (BD); 3≤d≤100, s≤230 2014 T42 Solution Treatment + Natural Aging (T42) ≥380 ≥220 ≥16
Cold drawn bar (BD); 3≤d≤100, s≤230 2014 T451 Solution heat-treated, stress-relieved by stretching (T451) ≥380 ≥220 ≥16
Cold drawn bar (BD); 3≤d≤100, s≤230 2014 T6 Solid Solution Heat Treatment + Artificial Aging (T6) ≥450 ≥380 ≥8
Cold drawn bar (BD); 3≤d≤100, s≤230 2014 T62 Solution Heat Treatment and Precipitation Heat Treatment (T62) ≥450 ≥380 ≥8
Cold drawn bar (BD); 3≤d≤100, s≤230 2014 T651 Solid Solution Heat Treatment + Stretching Stress Relief + Artificial Aging (T651) ≥450 ≥380 ≥8
① A50mm、A（5.65√S0）- gauge length，S0-Specimen area，s=S0，unit mm sq
② d-diameter、thickness or width across flats, unit mm；s - cross section area, unit mm sq
1 Approximate Comparison Table Wrought aluminum and aluminum alloy
China Japan United States International Organization for Standardization Germany European Standard
GB JIS ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. EN
2014 2014
A92014 		2014 A92014 AlCu4SiMgMn A92014 AlCu4SiMg 3.1255
A92014 		EN-AW-AlCu4SiMg
2 Approximate Comparison Table Aluminium and aluminium alloy
Japan United States International Organization for Standardization Germany European Standard United Kingdom
JIS ASTM ISO DIN EN/DIN W-Nr. EN Numerical Grade BS EN/BS
2014 AA2014 AlCu4SiMg AlCuSiMg 3.1255 ENAW-AlCu4SiMg ENAW-2014 L97
L98
2014 Corresponding Standards(Same grade name, different standards)
1 GB /T 3190-2008
2014
2 DIN 1725-1-1983
2014 AlCuSiMn 3.1255
3 GB /T 3190-2020
2014
4 JIS H 4040-2015
2014 A2014 BE A2014 BD
5 ISO 209-2007
2014 (AlCu4SiMg)
6 GB /T 3191-2019
2014
7 ASTM B275-2013
2014 CS41A A92014
8 GB /T 3880.1-2012
2014
9 JIS H 4000-2022
2014 A2014P