5083 A5083 BE A5083 BD - JIS H 4040-2015

Grade	5083
Other Names
Corresponding Standard	JIS H 4040-2015 Aluminium and aluminium alloy bars and wires
Classification	Aluminum and Aluminum Alloys
Properties	Corrosion Resistance Weldability

5083 Chemical Element Composition Content (%)

Component	Fe	Si	Mn	Cr	Cu	Ti	Zn	Mg	Other Individual	Other Total	More
Minimum Value	-	-	0.4	0.05	-	-	-	4	-	-	Al:余量
Maximum Value	0.4	0.4	1	0.25	0.1	0.15	0.25	4.9	0.05	0.15	Al:余量

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

5083 Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Extruded Rod (BE); d≤130, s≤200	A5083 O	Annealing (O)	275~355	≥110	A50mm ≥14
Extruded Rod (BE); d≤130, s≤200	A5083 H112	Strain - Only Hardening (H112)	≥275	≥110	≥12
Cold drawn bars/wires (BD/W); d≤3	A5083 O	Annealing (O)	275~355	-	-
Cold drawn bars/rods (BD/W); 3<d≤100		Annealing (O)	275~355	≥110	≥14
Cold drawn bars/wires (BD/W); d≤10	A5083 H111	Strain-Hardening (H111)	≥270	≥140	A ≥12
Cold drawn bars/wires (BD/W); d≤10	A5083 H12	Strain - Work hardened - 1/4 hard (H12)	≥300	≥200	≥4

① A50mm、A（5.65√S0）- gauge length，S0-Specimen area，s=S0，unit mm sq
② d-diameter、thickness or width across flats, unit mm；s - cross section area, unit mm sq

5083 Corresponding Standards(Same grade name, different standards)

1	GB /T 3190-2008
	5083
2	DIN 1725-1-1983
	5083 AlMg4.5Mn 3.3547
3	GB /T 3190-2020
	5083
4	JIS H 4040-2015
	5083 A5083 BE A5083 BD A5083 W
5	GB /T 3191-2019
	5083 (LF4)
6	ASME SB-928/SB-928M-2023
	5083
7	GB /T 3880.1-2012
	5083

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!