5086 A5086 BE A5086 BD - JIS H 4040-2015

Grade	5086
Other Names
Corresponding Standard	JIS H 4040-2015 Aluminium and Aluminium Alloy Bars and Wires
Classification	Aluminum and Aluminum Alloys

5086 Chemical Element Composition Content (%)

Component	Fe	Si	Mn	Cr	Cu	Ti	Zn	Mg	Other Individual	Other Total	More
Minimum Value	-	-	0.2	0.05	-	-	-	3.5	-	-	Al:余量
Maximum Value	0.5	0.4	0.7	0.25	0.1	0.15	0.25	4.5	0.05	0.15	Al:余量

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

5086 Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Extruded rod (BE); d≤200	A5086 O	Annealing (O)	240~320	≥95	A ≥18
Extruded bar (BE); d≤250	A5086 H112	Strain - Only Hardening (H112)	≥240	≥95	≥12
Cold-drawn bar (BE); d≤50	A5086 O	Annealing (O)	≥240	≥95	≥16
Cold Drawn Rod (BE); d≤25	A5086 H12	Strain-Hardening - 1/4 Hard (H12)	≥270	≥190	≥4
Cold Drawn Rod (BE); d≤25	A5086 H32	Strain-Hardening and Stabilization - 1/4 Hard (H32)	≥270	≥190	≥5

① A50mm、A（5.65√S0）- gauge length，S0-Specimen area，s=S0，unit mm sq
② d-diameter、thickness or width across flats, unit mm；s - cross section area, unit mm sq

Approximate Comparison Table Aluminium and Aluminium Alloy

Japan	United States	International Organization for Standardization	Germany		France	European Standard		Russia
JIS	ASTM	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	EN	Numerical Grade	GOST
5086	5086	AlMg4Mn	AlMg4Mn	3.3545	5086 A-G4MC	ENAW-AlMg4	ENAW-5086	AMg4 AMg4.5

5086 Corresponding Standards(Same grade name, different standards)

1	GB /T 3190-2008
	5086
2	DIN 1725-1-1983
	5086 AlMg4Mn 3.3545
3	GB /T 3190-2020
	5086
4	JIS H 4040-2015
	5086 A5086 BE A5086 BD
5	GB /T 3191-2019
	5086
6	ASME SB-928/SB-928M-2023
	5086
7	GB /T 3880.1-2012
	5086

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!