6005A A6005A BE - JIS H 4040-2015

Grade	6005A
Other Names
Corresponding Standard	JIS H 4040-2015 Aluminium and aluminium alloy bars and wires
Classification	Aluminum and Aluminum Alloys

6005A Chemical Element Composition Content (%)

Component	Fe	Si	Mn	Cr	Cu	Ti	Zn	Mg	Other Individual	Other Total	More
Minimum Value	-	0.5	-	-	-	-	-	0.4	-	-	Al:余量；Mn+Cr:0.12~0.5
Maximum Value	0.35	0.9	0.5	0.3	0.3	0.1	0.2	0.7	0.05	0.15	Al:余量；Mn+Cr:0.12~0.5

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

6005A Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Extruded bar (BE); d≤25	A6005A T6	Solid Solution Heat Treatment + Artificial Aging (T6)	≥270	≥225	A ≥10
Extruded Bar (BE); 25<d≤50		Solid Solution Heat Treatment + Artificial Aging (T6)	≥270	≥225	≥8
Extruded Bar (BE); 50<d≤100		Solid Solution Heat Treatment + Artificial Aging (T6)	≥260	≥215	≥8

① A50mm、A（5.65√S0）- gauge length，S0-Specimen area，s=S0，unit mm sq
② d-diameter、thickness or width across flats, unit mm；s - cross section area, unit mm sq

6005A Corresponding Standards(Same grade name, different standards)

1	GB /T 3190-2008
	6005A
2	DIN 1725-1-1983
	6005A AlMgSi0.7 3.3210
3	GB /T 3190-2020
	6005A
4	JIS H 4040-2015
	6005A A6005A BE
5	GB /T 3191-2019
	6005A

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!