6005C 6N01 A6005C BE A6N01 BE - JIS H 4040-2015

Grade	6005C
Other Names
Old Grade
Corresponding Standard	JIS H 4040-2015 Aluminium and Aluminium Alloy Bars and Wires
Classification	Aluminum and Aluminum Alloys

6005C Chemical Element Composition Content (%)

Component	Fe	Si	Mn	Cr	Cu	Ti	Zn	Mg	Other Individual	Other Total	More
Minimum Value	-	0.4	-	-	-	-	-	0.4	-	-	Al:余量；Mn+Cr≤0.5
Maximum Value	0.35	0.9	0.5	0.3	0.35	0.1	0.25	0.8	0.05	0.15	Al:余量；Mn+Cr≤0.5

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

6005C Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Extruded rod (BE); d≤6	A6005C T5	High-temperature deformation cooling + Artificial aging (T5)	≥245	≥205	A50mm ≥8
Extruded Bar (BE); 6<d≤12		High-temperature deformation cooling + Artificial aging (T5)	≥225	≥175	≥8
Extruded rod (BE); d≤6	A6005C T6	Solid Solution Heat Treatment + Artificial Aging (T6)	≥265	≥235	≥8

① A50mm、A（5.65√S0）- gauge length，S0-Specimen area，s=S0，unit mm sq
② d-diameter、thickness or width across flats, unit mm；s - cross section area, unit mm sq

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!