6060 A6060 BE A6060 BD - JIS H 4040-2015

Grade	6060
Other Names
Corresponding Standard	JIS H 4040-2015 Aluminium and aluminium alloy bars and wires
Classification	Aluminum and Aluminum Alloys

6060 Chemical Element Composition Content (%)

Component	Fe	Si	Mn	Cr	Cu	Ti	Zn	Mg	Other Individual	Other Total	More
Minimum Value	0.1	0.3	-	-	-	-	-	0.35	-	-	Al:余量
Maximum Value	0.3	0.6	0.1	0.05	0.1	0.1	0.15	0.6	0.05	0.15	Al:余量

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

6060 Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Extruded bar (BE); all sizes	6060 O	Annealing (O)	≤145	≥110	A50mm ≥16
Extruded bar (BE); all sizes	6060 T4	Solution Heat Treatment + Natural Aging (T4)	≥180	≥110	≥16
Extruded bar (BE); all sizes	6060 T451	Solution heat-treated, stress-relieved by stretching (T451)	≥180	≥110	≥16
Extruded bar (BE); all sizes	6060 T42	Solution Heat Treatment + Natural Aging (T42)	≥175	≥85	≥16
Extruded rod (BE); d≤6	6060 T6	Solid Solution Heat Treatment + Artificial Aging (T6)	≥260	≥240	≥8
Extruded bar (BE); d > 6		Solid Solution Heat Treatment + Artificial Aging (T6)	≥260	≥240	≥10
Extruded rod (BE); d≤6	6060 T62	Solution Heat Treatment and Precipitation Heat Treatment (T62)	≥260	≥240	≥8
Extruded bar (BE); d > 6		Solution Heat Treatment and Precipitation Heat Treatment (T62)	≥260	≥240	≥10
Extruded rod (BE); d≤6	6060 T6511	Solution Heat Treatment + Stress Relief + Artificial Aging (T6511)	≥260	≥240	≥8
Extruded bar (BE); d > 6		Solution Heat Treatment + Stress Relief + Artificial Aging (T6511)	≥260	≥240	≥10
Cold Drawn Rod (BD); d≤6	6060 T39	Strain-Hardening and Stabilizing - Extra Hard (H39)	≥270	-	-
Cold Drawn Bar (BD); d>6		Strain-Hardening and Stabilizing - Extra Hard (H39)	≥220	-	-
Cold drawn rod (BD); d≤80	6060 T4	Solution Heat Treatment + Natural Aging (T4)	≥130	≥65	≥13
Cold drawn rod (BD); d≤80	6060 T6	Solid Solution Heat Treatment + Artificial Aging (T6)	≥215	≥160	≥10
Cold Drawn Rod (BD); d≤6	6060 T89	Solution heat treatment + cold working + artificial aging (T89)	≥260	-	-

① A50mm、A（5.65√S0）- gauge length，S0-Specimen area，s=S0，unit mm sq
② d-diameter、thickness or width across flats, unit mm；s - cross section area, unit mm sq

6060 Corresponding Standards(Same grade name, different standards)

1	GB /T 3190-2008
	6060
2	DIN 1725-1-1983
	6060 AlMgSi 0.5 3.3206
3	GB /T 3190-2020
	6060
4	JIS H 4040-2015
	6060 A6060 BE A6060 BD
5	GB /T 3191-2019
	6060

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!