C2300 C2300 R C2300 RS - JIS H 3100-2018 - H2ABC

中文版

Grade	C2300
Other Names
Corresponding Standard	JIS H 3100-2018 Copper and copper alloy sheets, plates and strips
Classification	Copper and Copper Alloys
Properties	Corrosion Resistance Machinability

C2300 Chemical Element Composition Content (%)

Component	Fe	Cu	Pb	More
Minimum Value	-	84	-	Zn：余量
Maximum Value	0.05	86	0.05	Zn：余量

C2300 Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Elongation or Extension Rate δ %	Hardness HBW
Strip (R, RS); 0.3≤t≤3	C2300 R-O,C2300 RS-O	Annealing (O)	≥245	≥40	-
Plate (P); 0.3≤t≤30	C2300 P-O	Annealing (O)	≥245	≥40	-
Plate (P); 0.3≤t≤30	C2300 P-1/4H	1/4 Hard (1/4H)	275~355	≥28	-
Strip (R, RS); 0.3≤t≤3	C2300 R-1/4H,C2300 RS-1/4H	1/4 Hard (1/4H)	275~355	≥28	-
Plates (P); 0.3≤t≤20	C2300 P-1/2H	1/2 Hard (1/2H)	305~285	≥23	-
Strip (R, RS); 0.3≤t≤3	C2300 R-1/2H,C2300 RS-1/2H	1/2 Hard (1/2H)	305~285	≥23	-
Sheet (P); 0.3≤t≤10	C2300 P-H	Hard (H)	≥355	-	-
Strip (R, RS); 0.3≤t≤3	C2300 R-H,C2300 RS-H	Hard (H)	≥355	-	-

Approximate Comparison Table Brass

China	Japan	United States		International Organization for Standardization		Germany		European Standard		Russia
GB	JIS	ASTM	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	EN	Numerical Grade	GOST
H85	C2300	85Cu-15Zn	C23000	CuZn15	C23000	CuZn15	C23000 2.0240	CuZn15	CW502L	Л85

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!