中文版
Home Material BS 3100-1991
简体 | 繁體
Grade 304C12
Corresponding Standard BS 3100-1991
Specification for Steel Castings for General Engineering Purposes
Classification Cast Steel
Properties Corrosion Resistance
304C12 Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni
Minimum Value - - - - - 17 8
Maximum Value 0.03 1.5 2 0.04 0.04 21 12
304C12 Mechanical Properties
Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
%
ST(1000°C~1100°C) ≥430 1% proof stress Rp1.0 min ≥240
≥215		 ≥26
1 Approximate Comparison Table Corrosion-Resistant Cast Steels
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France Russia United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG03Cr18Ni10 C53043 SCS 19A SCS 19A SSC 19A CF3 J92500 GX2CrNiMo18-10 GX2CrNiMo19-11 1.4309 Z2CN18.10M 03Х18Н9Л 304C12
2 Approximate Comparison Table Corrosion-Resistant Cast Steels
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France Russia United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG03Cr18Ni10 C53043 SCS 19A SCS 36 SSC 19A CF3 J92500 GX2CrNi18-10 GX2CrNi19-11 1.4309 Z2CN18.10M 03Х18Н9Л 304C12
3 Approximate Comparison Table Corrosion-Resistant Cast Steels
China Japan United States Germany France Russia United Kingdom
GB JIS ASTM DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG00Cr18Ni10 SUS19 CF3 G-X2CrNi18 9 1.4306 Z2CN18.10M Х18Н8Л(旧号) 304C12
4 Approximate Comparison Table Heat-Resistant Cast Steels and Alloys
China Japan United States Germany France Russia United Kingdom
GB JIS ASTM UNS DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG00Cr18Ni10 SCS19 CF3 J92500 G-X2CrNi18 9 1.4036 Z2CN18.10M 03Х18Н11 304C12

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!