C72900 Cu-15Ni-8Sn - ASTM B740-2009(R2015) - H2ABC

中文版

Grade	C72900
Old Grade
Corresponding Standard	ASTM B740-2009(R2015) Copper-Nickel-Tin Spinodal Alloy Strip
Classification	Copper and Copper Alloys

C72900 Chemical Element Composition Content (%)

Component	Fe	Mn	Ni	Nb	Pb ^*	Zn	Sn	Mg	More
Minimum Value	-	-	14.5	-	-	-	7.5	-	Cu:余量
Maximum Value	0.5	0.3	15.5	0.1	0.02	0.5	8.5	0.15	Cu:余量

C72900 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Strip	Solution (TB00)	440~585	0.05% offset 165~275	≥32
Strip	Solution + cold working 1/4 hard (TD01)	515~690	0.05% offset 345~455	≥18
Strip	Solution + cold working 1/2 hard (TD02)	585~760	0.05% offset 450~580	≥8
Strip	Solution heat treatment + cold working hardening 3/4 hard (TD03)	655~825	0.05% offset 550~690	≥3
Strip	Solution + cold working hard (TD04)	690~895	0.05% offset 585~745	-
Strip	solution HT and Cold Worked Spring(TD08)	840~1000	0.05% offset 690~860	-
Strip	solution HT and Cold Worked Special Spring(TD12)	930~1070	0.05% offset 760~895	-
Strip	Spinodally HT(TX00)	825~1035	0.05% offset 655~825	≥6
Strip	1/4 Hard+Spinodal HT(TS01)	895~1105	0.05% offset 725~895	≥4
Strip	1/2 Hard+Spinodal HT(TS02)	1000~1205	0.05% offset 860~1035	≥3
Strip	3/4Hard+Spinodal HT(TS03)	1070~1275	0.05% offset 930~1105	≥2
Strip	Hard+Spinodal HT(TS04)	1140~1345	0.05% offset 1005~1170	≥2
Strip	Spring+Spinodal HT(TS08)	1205~1415	1070~1275	-
Strip	Special Spring+Spinodal HT(TS12)	1240~1550	1105~1380	-

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!