C35 1.0501 - NF EN 10083-2-2006

Grade	C35
	1.0501
Corresponding Standard	NF EN 10083-2-2006 Tempered non-alloy structural steel
Classification	Carbon Steel

C35 Chemical Element Composition Content (%)

Component	C ^①	Si	Mn	P	S	Cr	Ni	Mo	More
Minimum Value	0.32	-	0.5	-	-	-	-	-	Cr+Mo+Ni≤0.63 ①
Maximum Value	0.39	0.4	0.8	0.045	0.045	0.4	0.4	0.1	Cr+Mo+Ni≤0.63 ①

C35 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %
Steel: d ≤ 16mm; t ≤ 8mm	Quenching + Tempering (+QT)	630~780	≥430	≥17	≥40
Steel: 16mm ≤ d ≤ 40mm; 8mm ≤ t ≤ 20mm	Quenching + Tempering (+QT)	600~750	≥380	≥19	≥45
Steel: 40mm ≤ d ≤ 100mm; 20mm ≤ t ≤ 60mm	Quenching + Tempering (+QT)	550~700	≥320	≥20	≥50
Steel: d ≤ 16mm; t ≤ 16mm	Normalizing (+N)	≥550	≥300	≥18
Steel: 16mm ≤ d ≤ 100mm; 16mm ≤ t ≤ 100mm	Normalizing (+N)	≥520	≥270	≥19
Steel: 100mm ≤ d ≤ 250mm; 100mm ≤ t ≤ 250mm	Normalizing (+N)	≥500	≥245	≥19

1 Approximate Comparison Table

China	Japan	United States	International Organization for Standardization	Germany		France	European Standard		Russia	Sweden	United Kingdom
GB	JIS	ASTM	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	EN	Numerical Grade	GOST	SS	BS EN/BS
35	S35C	1035 Gr.1035	C35 C35E4	C35	1.0501	AF55C35 C35	C35	1.0501	35 40	1550	070M36 40HS

2 Approximate Comparison Table

China	Japan	United States	International Organization for Standardization	France	Russia	United Kingdom
GB	JIS	ASTM/AISI	ISO	NF EN/NF	GOST	BS EN/BS
GB/T 699-1999 35	S35C	1035	ISO 630-1:1987 C35 C35E4 C35M2	C35 XC35	35	060A35

3 Approximate Comparison Table

C35 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!