C35E 1.1181 XC38H1 - NF EN 10083-2-2006

Grade	C35E
	1.1181
Old Grade
Corresponding Standard	NF EN 10083-2-2006 Tempered non-alloy structural steel
Classification	Carbon Steel

C35E Chemical Element Composition Content (%)

Component	C ^①	Si	Mn	P	S ^②	Cr	Ni	Mo	More
Minimum Value	0.32	-	0.5	-	-	-	-	-	Cr+Mo+Ni≤0.63 ①
Maximum Value	0.39	0.4	0.8	0.03	0.035	0.4	0.4	0.1	Cr+Mo+Ni≤0.63 ①

C35E Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW	Impact Energy Absorption KV2 J
Steel: d ≤ 16mm; t ≤ 8mm	Quenching + Tempering (+QT)	630~780	≥430	≥17	≥40	HRC ① ≥48
Steel: 16mm ≤ d ≤ 40mm; 8mm ≤ t ≤ 20mm	Quenching + Tempering (+QT)	600~750	≥380	≥19	≥45	HRC ① ≥48	≥35
Steel: 40mm ≤ d ≤ 100mm; 20mm ≤ t ≤ 60mm	Quenching + Tempering (+QT)	550~700	≥320	≥20	≥50	HRC ① ≥48	≥35
Steel: d ≤ 16mm; t ≤ 16mm	Normalizing (+N)	≥550	≥300	≥18
Steel: 16mm ≤ d ≤ 100mm; 16mm ≤ t ≤ 100mm	Normalizing (+N)	≥520	≥270	≥19
Steel: 100mm ≤ d ≤ 250mm; 100mm ≤ t ≤ 250mm	Normalizing (+N)	≥500	≥245	≥19

Approximate Comparison Table

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

Russia

Sweden

United Kingdom

ISC

CNS

JIS

ASTM/AISI

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

U20352

S35C

SM35C

1035

G10350

C35E4

C35E
Ck35

1.1181

C35E
XC38

1572

C35E
080M36