Home Material BS 1449-2-1983
简体 | 繁體
Grade 405S17
Corresponding Standard BS 1449-2-1983
Steel plate, sheet and strip —Part 2: Specification for stainless and heat-resisting steel plate, sheet and strip
Classification Ferritic Stainless Steel
Properties Corrosion Resistance
405S17 Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni Al
Minimum Value - - - - - 12 - 0.1
Maximum Value 0.08 1 1 0.04 0.03 14 1 0.3
405S17 Mechanical Properties
thickness
t
mm		 Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Hardness
HBW
Thick Plate, Thin Plate, Strip; 0.3≤t<3 Softening Treatment ≥420 ≥245 ≥20 HV
≤175
Plate; 3≤t<100 Softening Treatment ≥420 ≥245 ≥20 HV
≤190
Narrow Strip; 0.05≤t<0.3 Softening Treatment ≥420 ≥245 ≥20 HV
≤175
1 Approximate Comparison Table Ferritic Stainless Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade SS BS EN/BS
06Cr13Al S11348 405 SUS 405 STS 405 405 S40500 X6CrAl 13 X6CrAl 13
(X7CrAl 13) 		1.4002 Z6CA 13 X6CrAl 13 1.4002 2302 405S17
2 Approximate Comparison Table Ferritic Heat-Resistant Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr13Al
(0Cr13Al) 		S11348 405 SUS 405 STR 405 405 S40500 X6CrAl 13
2
ISO 683-13-1986 		X6CrAl 13
(X7CrAl 13) 		1.4002 Z6CA 13 X6CrAl 13 1.4002 1Х20Ю 2302 405S17

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!