C10 1.0301 - DIN 1652-1963

Grade	C10
Germany W-Nr.	1.0301
Corresponding Standard	DIN 1652-1963 Bright non-alloy steel - Technical delivery conditions
Classification	Carbon Steel

C10 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	N ^*
Minimum Value	0.06	0.15	0.25	-	-	-
Maximum Value	0.12	0.35	0.5	0.045	0.045	0.01

C10 Mechanical Properties

thickness d mm	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
t≤5	C10 K	Cold Drawing + No Heat Treatment (K)	≥500	≥400	≥7
5<t≤10		Cold Drawing + No Heat Treatment (K)	≥500	≥360	≥8
10<t≤16		Cold Drawing + No Heat Treatment (K)	≥450	≥300	≥9
16<t≤25		Cold Drawing + No Heat Treatment (K)	≥400	≥250	≥10
25<t≤40		Cold Drawing + No Heat Treatment (K)	≥400	≥230	≥11
40<t≤100		Cold Drawing + No Heat Treatment (K)	≥340	≥180	≥12
t>100		Cold Drawing + No Heat Treatment (K)	≥340	≥180	≥12
All Sizes	C10 K+G；C10 SH+G	Cold Drawn + Softening Annealing (K+G) or Pickling + Softening (SH+G)				≤131 HB30

1 Approximate Comparison Table

China

Taiwan, China

Japan

South Korea

United States

Germany

France

Russia

Sweden

United Kingdom

ISC

CNS

JIS

ASTM/AISI

UNS

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

U20102

S10C

SM10C

1010

G10100

C10
Ck10

1.0301
1.1121

C10
XC10

1265

040A10
045M10

2 Approximate Comparison Table

C10 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!