CuZn38Pb0.5 2.0372 Ms60Pb - DIN 17671-1-1983

Grade	CuZn38Pb0.5
Germany W-Nr.	2.0372
Old Grade
Corresponding Standard	DIN 17671-1-1983 Wrought copper and copper alloys tube；Properties.
Classification	Copper and Copper Alloys
Properties	Forgability
Density	8.4 g/cm³

CuZn38Pb0.5 Chemical Element Composition Content (%)

Component	Fe	Ni	Cu	Pb	Al	Sn	Other Total	More
Minimum Value	-	-	59.5	0.3	-	-	-	Zn:余量
Maximum Value	0.3	0.3	61.5	1	0.05	0.2	0.2	Zn:余量

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

CuZn38Pb0.5 Mechanical Properties

thickness t mm	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Pipe; wall thickness as per agreement	2.0372.08	Extrusion or Hot Forged Tubes P (.08)	No specification	No specification	No specification	No specification
Pipes; t<10	2.0372.10	Soft F34 (.10)	≥340	≤220	≥35	≈80
Pipes; t<10	2.0372.26	Half Hard F41 (.26)	≥410	≥220	≥15	≈115
Pipes; t<5	2.0372.30	Hard F47 (.30)	≥470	≥350	≥10	≈140

Approximate Comparison Table Copper and Copper Alloy

Germany		European Standard
DIN EN/DIN	W-Nr.	EN	Numerical Grade
CuZn39Pb0.5	2.0372	CuZn39Pb0.5	CW610N

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!