简体 | 繁體
Grade X6CrAl 13
European Standard Steel Grade 1.4002
Corresponding Standard EN 10250-4-1999
Open die steel forgings for general engineering purposes - Part 4: Stainless steels
Classification Ferritic Stainless Steel
Properties Corrosion Resistance
X6CrAl 13 Chemical Element Composition Content (%)
Component C Si Mn P S * Cr Al
Minimum Value - - - - - 12 0.1
Maximum Value 0.08 1 1 0.04 0.03 14 0.3
X6CrAl 13 Mechanical Properties
thickness
t
mm		 Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa
t≤25 A 400~600 ≥230
1 Approximate Comparison Table Ferritic Stainless Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade SS BS EN/BS
06Cr13Al S11348 405 SUS 405 STS 405 405 S40500 X6CrAl 13 X6CrAl 13
(X7CrAl 13) 		1.4002 Z6CA 13 X6CrAl 13 1.4002 2302 405S17
2 Approximate Comparison Table Ferritic Heat-Resistant Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr13Al
(0Cr13Al) 		S11348 405 SUS 405 STR 405 405 S40500 X6CrAl 13
2
ISO 683-13-1986 		X6CrAl 13
(X7CrAl 13) 		1.4002 Z6CA 13 X6CrAl 13 1.4002 1Х20Ю 2302 405S17
X6CrAl13 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X6CrAl13 1.4002
2 EN 10250-4-1999
X6CrAl 13 1.4002
3 ISO TS 15510-2003
X6CrAl13
4 DIN 17440-1972
X6CrAl 13 X7CrAl 13 1.4002
5 ISO 15510-2014
X6CrAl13 4002-405-00-I

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!