CuSP 2.1498 - DIN 17671-1-1983

Grade	CuSP
Germany W-Nr.	2.1498
Corresponding Standard	DIN 17671-1-1983 Wrought copper and copper alloys tube；Properties.
Classification	Copper and Copper Alloys
Density	8.9 g/cm³

CuSP Chemical Element Composition Content (%)

Component	P	S	Other Total	More
Minimum Value	0.003	0.3	-	Cu:余量
Maximum Value	0.012	0.5	0.1	Cu:余量

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

CuSP Mechanical Properties

thickness t mm	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Pipe; wall thickness as per agreement	2.1498.08	Extrusion or Hot Forging P (.08)	No specification	No specification	No specification	No specification
Pipes; 4≤t＜12	2.1498.26	Half Hard F26 (.26)	≥260	≥200	≥8	≈85

Approximate Comparison Table Copper and Copper Alloy

Germany		European Standard
DIN EN/DIN	W-Nr.	EN	Numerical Grade
CuSP	2.1498	CuSP	CW114C

CuSP Corresponding Standards(Same grade name, different standards)

1	EN 12166-2016
	CuSP CW114C
2	DIN 17672-1-1983
	CuSP 2.1498
3	DIN 17671-1-1983
	CuSP 2.1498
4	DIN EN 12166-2016
	CuSP CW114C
5	DIN 17666-1983
	CuSP 2.1498

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!