CuTeP 2.1546 - DIN 17671-1-1983

Grade	CuTeP
Germany W-Nr.	2.1546
Corresponding Standard	DIN 17671-1-1983 Wrought copper and copper alloys tube；Properties.
Classification	Copper and Copper Alloys
Density	8.9 g/cm³

CuTeP Chemical Element Composition Content (%)

Component	P	Te	Other Total	More
Minimum Value	0.003	0.4	-	Cu:余量
Maximum Value	0.012	0.7	0.1	Cu:余量

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

CuTeP Mechanical Properties

thickness t mm	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Pipe; wall thickness as per agreement	2.1546.08	Extrusion or Hot Forging P (.08)	No specification	No specification	No specification	No specification
Pipes; 4≤t＜12	2.1546.26	Half Hard F26 (.26)	≥260	≥200	≥8	≈85

Approximate Comparison Table Cupper and cupper alloy

Germany		European Standard
DIN EN/DIN	W-Nr.	EN	Numerical Grade
CuTeP	2.1546	CuTeP	CW118C

CuTeP Corresponding Standards(Same grade name, different standards)

1	EN 12166-1998
	CuTeP CW118C
2	EN 12166-2016
	CuTeP CW118C
3	DIN 17672-1-1983
	CuTeP 2.1546
4	DIN 17671-1-1983
	CuTeP 2.1546
5	DIN EN 12166-2016
	CuTeP CW118C
6	DIN EN 12166-1998
	CuTeP CW118C
7	DIN 17666-1983
	CuTeP 2.1546

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!