Grade CuNi1P
Germany W-Nr. CW108C
Corresponding Standard DIN EN 12163-1998
Copper and copper alloys – Rod for general purposes
Classification Copper and Copper Alloys
Density 8.9 g/cm3
CuNi1P Chemical Element Composition Content (%)
Component P Ni Other Total More
Minimum Value 0.15 0.8 - Cu:余量
Maximum Value 0.25 1.2 0.1
"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.
CuNi1P Mechanical Properties
diameter/width across-flats
d
mm		 Mark
Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Hardness
HBW
2<d≤80 CuNi1P-R250 Solution Heat Treatment; R250 ≥250 ≈140* ≥20(A100)，
≥22(A11.3)，
≥25(A)
2<d≤80 CuNi1P-H065 Solution Heat Treatment; H065 HB: 65~95；
HV: 70~100
2<d≤25 CuNi1P-R500 Solution Heat Treatment + Cold Work; R500 ≥500 ≈430* ≥5(A100)，
≥6(A11.3)，
≥8(A)
2<d≤25 CuNi1P-H135 Solution Heat Treatment + Cold Work; H135 HB: 135~175；
HV: 140~180
25<d≤40 CuNi1P-R450 Solution Heat Treatment + Cold Work; R450 ≥450 ≈380* ≥10(A)
25<d≤40 CuNi1P-H125 Solution Heat Treatment + Cold Work; H125 HB: 125~175；
HV: 130~180
40<d≤80 CuNi1P-R400 Solution Heat Treatment + Cold Work; R400 ≥400 ≈330* ≥10(A)
40<d≤80 CuNi1P-H110 Solution Heat Treatment + Cold Work; H110 HB: 110~160；
HV: 115~165
2<d≤80 CuNi1P-R650 Solution Heat Treatment + Precipitation Hardening; R650 ≥650 ≈500* ≥8(A100)，
≥10(A11.3)，
≥12(A)
2<d≤80 CuNi1P-H190 Solution Heat Treatment + Precipitation Hardening; H190 HB: ≥190；
HV: ≥200
2<d≤25 CuNi1P-R800 Solution Heat Treatment + Cold Work + Precipitation Hardening; R800 ≥800 ≈730* ≥3*(A100)，
≥4*(A11.3)，
≥5(A)
2<d≤25 CuNi1P-H220 Solution Heat Treatment + Cold Work + Precipitation Hardening; H220 HB: ≥220；
HV: ≥230
25<d≤40 CuNi1P-R750 Solution Heat Treatment + Cold Work + Precipitation Hardening; R750 ≥750 ≈680* ≥5(A)
25<d≤40 CuNi1P-H210 Solution Heat Treatment + Cold Work + Precipitation Hardening; H210 HB: ≥210；
HV: ≥220
40<d≤80 CuNi1P-R700 Solution Heat Treatment + Cold Work + Precipitation Hardening; R700 ≥700 ≈630* ≥5(A)
40<d≤80 CuNi1P-H200 Solution Heat Treatment + Cold Work + Precipitation Hardening; H200 HB: ≥200；
HV: ≥210
2<d≤80 CuNi1P-M M No specification No specification No specification No specification
CuNi1P Corresponding Standards(Same grade name, different standards)
1 EN 12163-1998
CuNi1P CW108C
2 DIN EN 12163-1998
CuNi1P CW108C

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!