X1CrNiMoCu12-5-2 1.4422 - NF EN 10088-2-2005

Grade	X1CrNiMoCu12-5-2
	1.4422
Corresponding Standard	NF EN 10088-2-2005 Part2:Technical Delivery Conditions for Sheet/Plate and Strip of Corrosion Resisting Steels for General Purposes
Classification	Martensitic Stainless Steel

X1CrNiMoCu12-5-2 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	N
Minimum Value	-	-	-	-	-	11	4	0.2	1.3	-
Maximum Value	0.02	0.5	2	0.04	0.003	13	5	0.8	1.8	0.02

◎ Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All appropriate precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.

X1CrNiMoCu12-5-2 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW	Impact Energy Absorption KV2 J
Hot rolled strip steel: T ≤ 13.5mm	+A	750~950	≥550	T ≥ 3mm：≥ 15①	HRB：≤ 100 ; HB/HV：≤ 300	T ＞10mm：≥ 100
Hot rolled medium-thick plate: T ≤ 75mm	+QT650	750~950	≥550	T ≥ 3mm：≥ 15①	HV：≤ 300	T ＞10mm：≥ 100

◎ T-thickness；l-longitudinal；t-trasverse
◎ +A=soft annealed；+QT=quenched and tempered；+P=precipitation hardened；+AT=solutiong annealed；+SR=strength relieved

X1CrNiMoCu12-5-2 Corresponding Standards(Same grade name, different standards)

1	EN 10088-1-2005
	X1CrNiMoCu 12-5-2 1.4422
2	NF EN 10088-2-2005
	X1CrNiMoCu12-5-2 1.4422
3	NF EN 10088-1-2005
	X1CrNiMoCu12-5-2 1.4422

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!