X8CrNiS18-9 1.4305 - NF EN 10088-2-2005

Grade	X8CrNiS18-9
	1.4305
Corresponding Standard	NF EN 10088-2-2005 Part2:Technical Delivery Conditions for Sheet/Plate and Strip of Corrosion Resisting Steels for General Purposes
Classification	Austenitic Stainless Steel

X8CrNiS18-9 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	N
Minimum Value	-	-	-	-	0.15	17	8	-	-
Maximum Value	0.1	1	2	0.045	0.35	19	10	1	0.11

◎ Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All appropriate precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.

X8CrNiS18-9 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Hot rolled medium and thick plates: T ≤ 75mm	+AT	500~700	( t ) Rp0.2：≥ 190①③ Rp1.0：≥ 230①② ③	( t ) T＜3mm：≥35③④ T ≥ 3mm：≥35③⑤

◎ T-thickness；l-longitudinal；t-trasverse
◎ +A=soft annealed；+QT=quenched and tempered；+P=precipitation hardened；+AT=solutiong annealed；+SR=strength relieved

X8CrNiS18-9 Corresponding Standards(Same grade name, different standards)

1	EN 10088-1-2005
	X8CrNiS 18-9 1.4305
2	EN 10088-2-2005
	X8CrNiS18-9 1.4305
3	EN 10088-3-2005
	X8CrNiS18-9 1.4305
4	EN 10088-3-2014
	X8CrNiS18-9 1.4305
5	DIN EN 10088-3-2014
	X8CrNiS18-9 1.4305
6	NF EN 10088-2-2005
	X8CrNiS18-9 1.4305
7	NF EN 10088-1-2005
	X8CrNiS18-9 1.4305

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!