Home Material DIN EN 12163-1998
简体 | 繁體
Grade CuSi3Mn1
Germany W-Nr. CW116C
Corresponding Standard DIN EN 12163-1998
Copper and copper alloys – Rod for general purposes
Classification Copper and Copper Alloys
Density 8.8 g/cm3
CuSi3Mn1 Chemical Element Composition Content (%)
Component Fe Si Mn P Pb Al Zn Other Total More
Minimum Value - 2.7 0.7 - - - - - Cu:余量
Maximum Value 0.2 3.2 1.3 0.05 0.05 0.05 0.4 0.5
"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.
CuSi3Mn1 Mechanical Properties
diameter
d
mm		 Mark
Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Hardness
HBW
2<d≤75 CuSi3Mn1-R380 R380 ≥380 ≈260* ≥40(A100)，
≥45(A11.3)，
≥50(A)
2<d≤75 CuSi3Mn1-H085 H085 HB: 85~115；
HV: 90~120
2<d≤35 CuSi3Mn1-R425 R425 ≥425 ≈290* ≥30(A100)，
≥33(A11.3)，
≥36(A)
35<d≤75 CuSi3Mn1-R425 R425 ≥425 ≈290* ≥32(A)
2<d≤75 CuSi3Mn1-H110 H110 HB: 110~145；
HV: 115~150
2<d≤35 CuSi3Mn1-R495 R495 ≥495 ≈350* ≥22(A100)，
≥25(A11.3)，
≥28(A)
35<d≤75 CuSi3Mn1-R495 R495 ≥495 ≈350* ≥24(A)
2<d≤75 CuSi3Mn1-H130 H130 HB: 130~165；
HV: 135~170
2<d≤35 CuSi3Mn1-R620 R620 ≥620 ≈500* ≥12(A100)，
≥14(A11.3)，
≥16(A)
35<d≤75 CuSi3Mn1-R620 R620 ≥620 ≈500* ≥14(A)
2<d≤75 CuSi3Mn1-H150 H150 HB: 150~185；
HV: 155~190
2<d≤12 CuSi3Mn1-R790 R790 ≥790 ≈750* ≥6(A100)，
≥7(A11.3)，
≥8(A)
2<d≤12 CuSi3Mn1-H180 H180 HB: ≥180；
HV: ≥190
2<d≤6 CuSi3Mn1-R900 R900 ≥900 ≈890* ≥3*(A100)，
≥4*(A11.3)
2<d≤6 CuSi3Mn1-H210 H210 HB: ≥210；
HV: ≥220
2<d≤75 CuSi3Mn1-M M No specification No specification No specification No specification
CuSi3Mn1 Corresponding Standards(Same grade name, different standards)
1 EN 12163-1998
CuSi3Mn1 CW116C
2 EN 12166-1998
CuSi3Mn1 CW116C
3 DIN EN 12163-1998
CuSi3Mn1 CW116C
4 DIN EN 12166-1998
CuSi3Mn1 CW116C

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!