Home Material NF EN 10028-7-2008
简体 | 繁體
Grade X6CrNiTi18-10
1.4541
Corresponding Standard NF EN 10028-7-2008
Flat products made of steels for pressure purposes - Part 7 : stainless steels
Classification Austenitic Stainless Steel
X6CrNiTi18-10 Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni More
Minimum Value - - - - - 17 9 Ti:5×C~0.7
Maximum Value 0.08 1 2 0.045 0.015 19 12
◎ Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.
X6CrNiTi18-10 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Impact Energy Absorption
KV2
J
C：T ≤ 8 +AT 520~720 Rp0.2：≥220
Rp1.0：≥250
①②		 T ＜ 3mm: ≥40
T ≥ 3mm: ≥ 40
②③		 20℃：
(l: ≥100；t: ≥60)
-196℃：
(t: ≥60)
H：T ≤ 13.5 +AT 520~720 Rp0.2：≥200
Rp1.0：≥240
①②		 T ＜ 3mm: ≥40
T ≥ 3mm: ≥ 40
②③		 20℃：
(l: ≥100；t: ≥60)
-196℃：
(t: ≥60)
P：T ≤ 75 +AT 500~700 Rp0.2：≥200
Rp1.0：≥240
①②		 T ＜ 3mm: ≥40
T ≥ 3mm: ≥ 40
②③		 20℃：
(l: ≥100；t: ≥60)
-196℃：
(t: ≥60)
Steel: 20℃ ⑤ - ≥500 Rp0.2：≥200
Rp1.0：≥240
≥40 -
Steel: -80℃ ⑤ - ≥855 Rp0.2：≥260
Rp1.0：≥290
≥35 -
Steel: -150℃ ⑤ - ≥1100 Rp0.2：≥350
Rp1.0：≥420
≥35 -
Steel: -196℃ ⑤ - ≥1200 Rp0.2：≥390
Rp1.0：≥470
≥30 -
◎ C-Cold rolled strip；H-Hot rolled strip；P-Hot rolled plate；T-Thickness；t-transverse；l-Longitudinal
◎ +A=annealed；+AT=solution annealed；+QT = quenched and tempered；+RA=recrystallizing annealed condition
X6CrNiTi18-10 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X6CrNiTi 18-10 1.4541
2 EN 10296-2-2005
X6CrNiTi18-10 1.4541
3 EN 10253-4-2003
X6CrNiTi18-10 1.4541
4 EN 10263-5-2001
X6CrNiTi18-10 1.4541
5 EN 10250-4-1999
X6CrNiTi 18-10 1.4541
6 ISO TS 15510-2003
X6CrNiTi18-10
7 EN 10088-2-2005
X6CrNiTi18-10 1.4541
8 EN 10088-3-2005
X6CrNiTi 18-10 1.4541
9 ISO 9327(-5)-1999
X6CrNiTi18-10 (F53)
10 EN 10088-3-2014
X6CrNiTi 18-10 1.4541
11 ISO 15510-2014
X6CrNiTi18-10 4541-321-00-I
12 DIN EN 10263-5-2018
X6CrNiTi18-10 1.4541
13 ISO 9328-7-2018
X6CrNiTi18-10
14 DIN EN 10088-3-2014
X6CrNiTi 18-10 1.4541
15 ISO 683-18-2014
X6CrNiTi18-10 4541-321-00-I
16 ISO 4954-2018
X6CrNiTi18-10 4541-321-00-I
17 NF EN 10088-2-2005
X6CrNiTi18-10 1.4541
18 NF EN 10088-1-2005
X6CrNiTi18-10 1.4541
19 NF EN 10028-7-2008
X6CrNiTi18-10 1.4541
20 NF EN 10296-2-2005
X6CrNiTi18-10 1.4541
21 NF EN 10028-7-2000
X6CrNiTi18-10 1.4541
22 EN 10263-5-2017
X6CrNiTi18-10 1.4541
23 ISO 4954-2-2024
X6CrNiTi18-10 4541-321-00-I
24 DIN EN 10296-2-2006
X6CrNiTi18-10 1.4541

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!