Home Material NF EN 10028-7-2008
简体 | 繁體
Grade X5CrNiMo17-12-2
1.4401
Corresponding Standard NF EN 10028-7-2008
Flat Products Made of Steels for Pressure Purposes - Part 7 : Stainless Steels
Classification Austenitic Stainless Steel
X5CrNiMo17-12-2 Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni Mo N
Minimum Value - - - - - 16.5 10 2 -
Maximum Value 0.07 1 2 0.045 0.015 18.5 13 2.5 0.1
◎ Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.
X5CrNiMo17-12-2 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Impact Energy Absorption
KV2
J
C：T ≤ 8 +AT 530~680 Rp0.2：≥240
Rp1.0：≥270
①②		 T ＜ 3mm: ≥40
T ≥ 3mm: ≥ 40
②③		 20℃：
(l: ≥100；t: ≥60)
-196℃：
(t: ≥60)
H：T ≤ 13.5 +AT 530~680 Rp0.2：≥220
Rp1.0：≥260
①②		 T ＜ 3mm: ≥40
T ≥ 3mm: ≥ 40
②③		 20℃：
(l: ≥100；t: ≥60)
-196℃：
(t: ≥60)
P：T ≤ 75 +AT 520~670 Rp0.2：≥220
Rp1.0：≥260
①②		 T ＜ 3mm: ≥45
T ≥ 3mm: ≥ 45
②③		 20℃：
(l: ≥100；t: ≥60)
-196℃：
(t: ≥60)
◎ C-Cold rolled strip；H-Hot rolled strip；P-Hot rolled plate；T-Thickness；t-transverse；l-Longitudinal
◎ +A=annealed；+AT=solution annealed；+QT = quenched and tempered；+RA=recrystallizing annealed condition
X5CrNiMo17-12-2 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X5CrNiMo 17-12-2 1.4401
2 EN 10296-2-2005
X5CrNiMo17-12-2 1.4401
3 EN 10253-4-2003
X5CrNiMo17-12-2 1.4401
4 EN 10263-5-2001
X5CrNiMo17-12-2 1.4401
5 EN 10269-2006
X5CrNiMo17-12-2 1.4401
6 EN 10250-4-1999
X5CrNiMo 17-12-2 1.4401
7 ISO TS 15510-2003
X5CrNiMo17-12-2
8 EN 10088-2-2005
X5CrNiMo17-12-2 1.4401
9 DIN 17440-1972
X5CrNiMo 17-12-2 X5CrNiMo 18-10 1.4401
10 EN 10088-3-2005
X5CrNiMo17-12-2 1.4401
11 EN 10297(2)-2005
X5CrNiMo17-12-2 1.4401
12 EN 10269-2013
X5CrNiMo 17-12-2 1.4401
13 EN 10088-3-2014
X5CrNiMo17-12-2 1.4401
14 ISO 15510-2014
X5CrNiMo17-12-2 4401-316-00-I
15 NF EN 10269-1999
X5CrNiMo17-12-2 1.4401
16 VDI 2230-1-2015
X5CrNiMo 17-12-2 1.4401
17 DIN EN 10263-5-2018
X5CrNiMo 17-12-2 1.4401
18 DIN EN 10269-2014
X5CrNiMo 17-12-2 1.4401
19 ISO 9328-7-2018
X5CrNiMo17-12-2
20 DIN EN 10088-3-2014
X5CrNiMo17-12-2 1.4401
21 DIN EN 10270-3-2012
X5CrNiMo17-12-2 1.4401
22 ISO 683-18-2014
X5CrNiMo17-12-2 4401-316-00-I
23 ISO 4954-2018
X5CrNiMo17-12-2 4401-316-00-I
24 NF EN 10088-2-2005
X5CrNiMo17-12-2 1.4401
25 NF EN 10088-1-2005
X5CrNiMo17-12-2 1.4401
26 NF EN 10028-7-2008
X5CrNiMo17-12-2 1.4401
27 NF EN 10296-2-2005
X5CrNiMo17-12-2 1.4401
28 NF EN 10028-7-2000
X5CrNiMo17-12-2 1.4401
29 EN 10263-5-2017
X5CrNiMo 17-12-2 1.4401 SS316
30 DIN EN 10151-2002
X5CrNiMo17-12-2 1.4401
31 ISO 4954-2-2024
X5CrNiMo17-12-2 4401-316-00-I
32 DIN EN 10296-2-2006
X5CrNiMo17-12-2 1.4401
33 EN 10272-2016
X5CrNiMo17-12-2 1.4401
34 EN 10217-7-2021
X5CrNiMo 17-12-2 1.4401
35 EN 10088-2-2024
X5CrNiMo17-12-2 1.4401
36 EN 10028-7-2016
X5CrNiMo17-12-2 1.4401

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!