Grade EN AW-5154A [Al Mg3.5(A)]
Corresponding Standard DIN EN 754-2-2017
Aluminium and Aluminium Alloys — Cold Drawn Rod/Bar and Tube — Part 2: Mechanical Properties
Classification Aluminum and Aluminum Alloys
EN AW-5154A [Al Mg3.5(A)] Chemical Element Composition Content (%)
Component Fe Si Be * Mn Cr Cu Ti Zn Mg Other Individual Other Total More
Minimum Value - - - - - - - - 3.1 - - Al:余量； Mn+Cr:0.1~0.5
Maximum Value 0.5 0.5 0.0003 0.5 0.25 0.1 0.2 0.2 3.9 0.05 0.15
"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.
EN AW-5154A [Al Mg3.5(A)] Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Hardness
HBW
Cold drawn bar; d≤80,s≤60 O，H111 200~260 ≥85 ≥16(A)；
≥14(A50)		 55
Cold drawn bars; d ≤ 25 Strain-hardening - 1/2 Hard (H14);
Strain-hardening + incomplete annealing - 1/2 hard (H24);
Strain-hardening + stabilization - 1/2 hard (H34)		 260~320 ≥200 ≥5(A)；
≥4(A50)		 75
Cold drawn bars; d ≤ 10 Strain-hardening - 4/4 Hard (H18);
Strain-hardening + incomplete annealing - 4/4 hard (H28);
Strain-hardening + stabilization - 4/4 hard (H38)		 ≥310 ≥240 ≥3(A)；
≥2(A50)		 80
Cold drawn pipe; t≤20 O，H111 200~260 ≥85 ≥16(A)；
≥14(A50)		 55
Cold drawn pipe; t≤10 Strain-hardening - 1/2 Hard (H14);
Strain-hardening + incomplete annealing - 1/2 hard (H24);
Strain-hardening + stabilization - 1/2 hard (H34)		 260~320 ≥200 ≥5(A)；
≥4(A50)		 75
Cold drawn pipes; t≤5 Strain-hardening - 4/4 Hard (H18);
Strain-hardening + incomplete annealing - 4/4 hard (H28);
Strain-hardening + stabilization - 4/4 hard (H38)		 ≥310 ≥240 ≥3(A)；
≥2(A50)		 80

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!