X6CrNi25-20 1.4951 - NF EN 10028-7-2008

Grade	X6CrNi25-20
	1.4951
Corresponding Standard	NF EN 10028-7-2008 Flat products made of steels for pressure purposes - Part 7 : stainless steels
Classification	Austenitic Stainless Steel

X6CrNi25-20 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	N
Minimum Value	0.04	-	-	-	-	24	19	-
Maximum Value	0.08	0.7	2	0.035	0.015	26	22	0.1

◎ Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.

X6CrNi25-20 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Impact Energy Absorption KV2 J
C：T ≤ 8	+AT	530~730	R_p0.2：≥220 R_p1.0：≥250 ①②	T ＜ 3mm: ≥35 T ≥ 3mm: ≥ 35 ②③	20℃： (l: ≥100；t: ≥60)
H：T ≤ 13.5	+AT	510~710	R_p0.2：≥200 R_p1.0：≥240 ①②	T ＜ 3mm: ≥35 T ≥ 3mm: ≥ 35 ②③	20℃： (l: ≥100；t: ≥60)
P：T ≤ 75	+AT	510~710	R_p0.2：≥200 R_p1.0：≥240 ①②	T ＜ 3mm: ≥35 T ≥ 3mm: ≥ 35 ②③	20℃： (l: ≥100；t: ≥60)

◎ C-Cold rolled strip；H-Hot rolled strip；P-Hot rolled plate；T-Thickness；t-transverse；l-Longitudinal
◎ +A=annealed；+AT=solution annealed；+QT = quenched and tempered；+RA=recrystallizing annealed condition

X6CrNi25-20 Corresponding Standards(Same grade name, different standards)

1	EN 10088-1-2005
	X6CrNi 25-20 1.4951
2	EN 10302-2008
	X6CrNi 25-20 1.4951
3	EN 10269-2013
	X6CrNi 25-20 1.4951
4	ISO 15510-2014
	X6CrNi25-20 4951-310-08-I
5	DIN EN 10269-2014
	X6CrNi 25-20 1.4951
6	ISO 9328-7-2018
	X6CrNi25-20
7	EU 95-1979
	X6CrNi 25-20
8	NF EN 10088-1-2005
	X6CrNi25-20 1.4951
9	NF EN 10028-7-2008
	X6CrNi25-20 1.4951
10	NF EN 10028-7-2000
	X6CrNi25-20 1.4951

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!