X8CrNiNb16-13 1.4961 - NF EN 10028-7-2008

Grade	X8CrNiNb16-13
	1.4961
Corresponding Standard	NF EN 10028-7-2008 Flat products made of steels for pressure purposes - Part 7 : stainless steels
Classification	Austenitic Stainless Steel

X8CrNiNb16-13 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	More
Minimum Value	0.04	0.3	-	-	-	15	12	Nb:10×C~1.2
Maximum Value	0.1	0.6	1.5	0.035	0.015	17	14	Nb:10×C~1.2

◎ Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.

X8CrNiNb16-13 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Impact Energy Absorption KV2 J
P：T ≤ 75	+AT	510~690	R_p0.2：≥200 R_p1.0：≥240 ①②	T ＜ 3mm: ≥35 T ≥ 3mm: ≥ 35 ②③	20℃： (l: ≥100；t: ≥60)

◎ C-Cold rolled strip；H-Hot rolled strip；P-Hot rolled plate；T-Thickness；t-transverse；l-Longitudinal
◎ +A=annealed；+AT=solution annealed；+QT = quenched and tempered；+RA=recrystallizing annealed condition

X8CrNiNb16-13 Corresponding Standards(Same grade name, different standards)

1	EN 10088-1-2005
	X8CrNiNb 16-13 1.4961
2	EN 10302-2008
	X8CrNiNb 16-13 1.4961
3	ISO 15510-2014
	X8CrNiNb16-13 4961-347-77-E
4	ISO 9328-7-2018
	X8CrNiNb16-13
5	ISO 4955-2016
	X8CrNiNb16-13 4961-347-77-E
6	NF EN 10088-1-2005
	X8CrNiNb16-13 1.4961
7	NF EN 10028-7-2008
	X8CrNiNb16-13 1.4961
8	NF EN 10028-7-2000
	X8CrNiNb16-13 1.4961

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!