Z8CN25-20 - NF A 35-578-1991

Grade	Z8CN25-20
Corresponding Standard	NF A 35-578-1991 Iron and Steel. Stainless Steel for High Temperature Application
Classification	Austenitic Stainless Steel

Z8CN25-20 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni
Minimum Value	-	-	-	-	-	24	19
Maximum Value	0.08	0.75	2	0.035	0.015	26	21

Z8CN25-20 Mechanical Properties

Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
+Q1050~1100	500~750	≥210	≥35	≤192

Approximate Comparison Table Austenitic Heat-Resistant Steel

China	Japan	United States		International Organization for Standardization	Germany	France	European Standard		Russia	Sweden	United Kingdom
GB	JIS	ASTM	UNS	ISO	DIN EN/DIN	NF EN/NF	EN	Numerical Grade	GOST	SS	BS EN/BS
1Cr25Ni20Si2	SUS310S	310S	S31008	H16	X8CrNi25-21	Z8CN25-20	X8CrNi25-21	1.4845	10KH23N18 20KH23N18	2361	310S16 310S24 310S31

Z8CN25-20 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!