NiFe25Cr20NbTi 2.4955 - NF EN 10090-1998

Grade	NiFe25Cr20NbTi
	2.4955
Corresponding Standard	NF EN 10090-1998 Valve steels and alloys for internal combustion engines
Classification	Nickel and Nickel Alloys
Density	8.1 g/cm³

NiFe25Cr20NbTi Chemical Element Composition Content (%)

Component	Fe	C	Si	Mn	P	S	Cr	Ti	B	Al	More
Minimum Value	23	0.04	-	-	-	-	18	1	-	0.3	Ni:余量 Nb+Ta:1~2
Maximum Value	28	0.1	1	1	0.03	0.015	21	2	0.008	1	Ni:余量 Nb+Ta:1~2

◎ Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser, excpet for finishing the cast. All appropriate measures shall be taken to prevent the addition of these elements from scrap or other materials used in steelmaking ,which may adversely affect the mechanical properties and usability .

NiFe25Cr20NbTi Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW
Steel:	+Q930~1030	≤1000				HB: ≤ 295
Steel: d≤40	+AT+P	900 to 1100	500 ①	25 ①	30 ①	HRC:28 ①

◎ d=thickness；+A=soft annealed；+Q=quenched；+P=precipitation hardened；+AT=solution annealed；+QT=quenched and tempered；The suffix number after the heat treatment symbol indicates the temperature in °C.

NiFe25Cr20NbTi Corresponding Standards(Same grade name, different standards)

1	ISO 683-15-1992
	NiFe 25 Cr 20 NbTi
2	NF EN 10090-1998
	NiFe25Cr20NbTi 2.4955

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!