CuBe2 CW101C - EN 1654-1998

Grade	CuBe2
European Standard Steel Grade	CW101C
Corresponding Standard	EN 1654-1998 Copper and copper alloys - Strip for springs and connectors
Classification	Copper and Copper Alloys
Density	8.3 g/cm³

CuBe2 Chemical Element Composition Content (%)

Component	Fe	Be	Ni	Co	Other Total	More
Minimum Value	-	1.8	-	-	-	Cu:余量
Maximum Value	0.2	2.1	0.3	0.3	0.5	Cu:余量

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

CuBe2 Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW	Bending Strength σ_w Mpa
Strip	CuBe2-R410	Solution heat treatment + cold rolling R410	410~530		≥35ⓐ ；≥35ⓑ
Strip	CuBe2-H090	Solution heat treatment + cold rolling H090				HV: 90~150
Strip	CuBe2-Y190	Solution heat treatment + cold rolling Y190		190~(380)	≥35ⓐ ；≥35ⓑ
Strip	CuBe2-R1130	Solution treatment + cold rolling + precipitation hardening R1130	1130~1350		≥3ⓐ ；≥3ⓑ
Strip	CuBe2-H350	Solution treatment + cold rolling + precipitation hardening H350				HV: 350~410
Strip	CuBe2-Y960	Solution treatment + cold rolling + precipitation hardening Y960		960~(1210)	≥3ⓐ ；≥3ⓑ
Strip	CuBe2-B770	Solution treatment + cold rolling + precipitation hardening B770				HV: (350)~(410)	Bending limit ≥770
Strip	CuBe2-R510	Solution heat treatment + cold rolling R510	510~610		≥15ⓐ ；≥15ⓑ
Strip	CuBe2-H120	Solution heat treatment + cold rolling H120				HV: 120~190
Strip	CuBe2-Y410	Solution heat treatment + cold rolling Y410		410~(560)	≥15ⓐ ；≥15ⓑ
Strip	CuBe2-R1190	Solution treatment + cold rolling + precipitation hardening R1190	1190~1420		≥3ⓐ ；≥3ⓑ
Strip	CuBe2-H360	Solution heat treatment + cold rolling + precipitation hardening H360				HV: 360~430
Strip	CuBe2-Y1020	Solution treatment + cold rolling + precipitation hardening Y1020		1020~(1280)	≥3ⓐ ；≥3ⓑ
Strip	CuBe2-B820	Solution treatment + cold rolling + precipitation hardening B820				HV: (360)~(430)	Bending limit ≥820
Strip	CuBe2-R580	Solution heat treatment + cold rolling R580	580~690		≥8ⓐ ；≥8ⓑ
Strip	CuBe2-H170	Solution treatment + cold rolling H170				HV: 170~220
Strip	CuBe2-Y510	Solution heat treatment + cold rolling Y510		510~(660)	≥8ⓐ ；≥8ⓑ
Strip	CuBe2-R1270	Solution treatment + cold rolling + precipitation hardening R1270	1270~1490
Strip	CuBe2-H370	Solution treatment + cold rolling + precipitation hardening H370				HV: 370~440
Strip	CuBe2-Y1100	Solution treatment + cold rolling + precipitation hardening Y1100		1100~(1350)
Strip	CuBe2-B880	Solution treatment + cold rolling + precipitation hardening B880				HV: (370)~(440)	Bending limit ≥880
Strip	CuBe2-R680	Solution heat treatment + cold rolling R680	680~830		≥2ⓐ ；≥2ⓑ
Strip	CuBe2-H220	Solution treatment + cold rolling H220				HV: 220~290
Strip	CuBe2-Y620	Solution heat treatment + cold rolling Y620		620~(800)	≥2ⓐ ；≥2ⓑ
Strip	CuBe2-R1310	Solution treatment + cold rolling + precipitation hardening R1310	1310~1520
Strip	CuBe2-H380	Solution treatment + cold rolling + precipitation hardening H380				HV: 380~450
Strip	CuBe2-Y1130	Solution treatment + cold rolling + precipitation hardening Y1130		1130~(1420)
Strip	CuBe2-B920	Solution treatment + cold rolling + precipitation hardening B920				HV: (380)~(450)	Bending limit ≥920
Strip	CuBe2-R690	R690*	690~760		≥16ⓐ ；≥16ⓑ
Strip	CuBe2-H210	H210*				HV: 210~250
Strip	CuBe2-Y480	Y480*		480~(660)	≥16ⓐ ；≥16ⓑ
Strip	CuBe2-B400	B400*				HV: (210)~(250)	Bending limit ≥400
Strip	CuBe2-R750	R750*	750~830		≥15ⓐ ；≥15ⓑ
Strip	CuBe2-H230	H230*				HV: 230~280
Strip	CuBe2-Y550	Y550*		550~(760)	≥15ⓐ ；≥15ⓑ
Strip	CuBe2-B500	B500*				HV: (230)~(280)	Bending limit ≥500
Strip	CuBe2-R820	R820*	820~930		≥12ⓐ ；≥12ⓑ
Strip	CuBe2-H250	H250*				HV: 250~310
Strip	CuBe2-Y650	Y650*		650~(870)	≥12ⓐ ；≥12ⓑ
Strip	CuBe2-B530	B530*				HV: (250)~(310)	Bending limit ≥530
Strip	CuBe2-R930	R930*	930~1040		≥9ⓐ ；≥9ⓑ
Strip	CuBe2-H280	H280*				HV: 280~350
Strip	CuBe2-Y750	Y750*		750~(940)	≥9ⓐ ；≥9ⓑ
Strip	CuBe2-B600	B600*				HV: (280)~(350)	Bending limit ≥600

1 Approximate Comparison Table Processing of High Copper Alloys

China		Japan	United States		International Organization for Standardization		Germany		European Standard		Russia
GB	ISC	JIS	ASTM	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	EN	Numerical Grade	GOST
TBe2 QBe2	T17720	C1720 C17200	97.8Cu-1.9Be-.3Co	C17200	CuBe2	C17200	CuBe2	C17200 2.1247	CuBe2	CW101C	БрБН2

2 Approximate Comparison Table Copper and Copper Alloy

Germany		European Standard
DIN EN/DIN	W-Nr.	EN	Numerical Grade
CuBe2	2.1247	CuBe2	CW101C

CuBe2 Corresponding Standards(Same grade name, different standards)

1	EN 12163-1998
	CuBe2 CW101C
2	EN 12166-1998
	CuBe2 CW101C
3	EN 1654-1998
	CuBe2 CW101C
4	EN 12166-2016
	CuBe2 CW101C
5	DIN 17672-1-1983
	CuBe2 2.1247
6	DIN EN 12163-1998
	CuBe2 CW101C (2.1247)
7	DIN EN 12163-2016
	CuBe2 CW101C
8	DIN EN 12166-2016
	CuBe2 CW101C
9	DIN EN 12166-1998
	CuBe2 CW101C
10	DIN 17666-1983
	CuBe2 2.1247
11	EN 12163-2016
	CuBe2 CW101C
12	DIN 2076-1984
	CuBe2
13	EN 12167-2024
	CuBe2 CW101C

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!