CuAl6Si2Fe CW301G - EN 12163-1998

Grade	CuAl6Si2Fe
European Standard Steel Grade	CW301G
Corresponding Standard	EN 12163-1998 Copper and copper alloys — Rod for general purposes
Classification	Copper and Copper Alloys
Density	7.7 g/cm³

CuAl6Si2Fe Chemical Element Composition Content (%)

Component	Fe	Si	Mn	Ni	Pb	Al	Zn	Sn	Other Total	More
Minimum Value	0.5	2	-	-	-	6	-	-	-	Cu:余量
Maximum Value	0.7	2.4	0.1	0.1	0.05	6.4	0.4	0.1	0.2	Cu:余量

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

CuAl6Si2Fe Mechanical Properties

diameter/width across-flats d mm	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
5<d≤80	CuAl6Si2Fe-R500	R500	≥500	≈250*	≥18(A11.3)， ≥20(A)
5<d≤80	CuAl6Si2Fe-H120	H120				HB: 120~150； HV: 125~155
5<d≤40	CuAl6Si2Fe-R600	R600	≥600	≈350*	≥10(A11.3)， ≥12(A)
5<d≤40	CuAl6Si2Fe-H140	H140				HB: ≥140； HV: ≥145
5<d≤80	CuAl6Si2Fe-M	M	No specification	No specification	No specification	No specification

① Material condition names and designations:
H - Hardness (Brinell hardness or Vickers hardness), with the suffix number indicating the hardness value.
R - Tensile strength, with the suffix number indicating the minimum tensile strength value.
M - Manufactured without specified mechanical properties. Refer to standard EN 1173-2008.
② A100, A11.3, A - Gauge length.

CuAl6Si2Fe Corresponding Standards(Same grade name, different standards)

1	EN 12163-1998
	CuAl6Si2Fe CW301G
2	DIN EN 12163-1998
	CuAl6Si2Fe CW301G

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!