X4CrNiMo16-5-1 1.4418 - NF EN 10028-7-2000

Grade	X4CrNiMo16-5-1
	1.4418
Corresponding Standard	NF EN 10028-7-2000 Flat products made of steels for pressure purposes Part 7: Stainless steels
Classification	Martensitic Stainless Steel

X4CrNiMo16-5-1 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo	N
Minimum Value	-	-	-	-	-	15	4	0.8	0.02
Maximum Value	0.06	0.7	1.5	0.04	0.015	17	6	1.5	-

◎ Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.

X4CrNiMo16-5-1 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Impact Energy Absorption KV2 J
P：T ≤ 75	+QT	840~980	≥680	T ≥3mm：14 ①	20℃: ≥ 55 -20℃: ≥ 40

◎ C-Cold rolled strip；H-Hot rolled strip；P-Hot rolled plate；T-Thickness；t-transverse；l-Longitudinal
◎ +A=annealed；+AT=solution annealed；+QT = quenched and tempered；+RA=recrystallizing annealed condition

X4CrNiMo16-5-1 Corresponding Standards(Same grade name, different standards)

1	EN 10088-1-2005
	X4CrNiMo 16-5-1 1.4418
2	EN 10250-4-1999
	X4CrNiMo16-5-1 1.4418
3	EN 10088-3-2005
	X4CrNiMo16-5-1 1.4418
4	EN 10088-3-2014
	X4CrNiMo16-5-1 1.4418
5	ISO 15510-2014
	X4CrNiMo16-5-1 4418-431-77-E
6	ISO 9328-7-2018
	X4CrNiMo16-5-1
7	DIN EN 10088-3-2014
	X4CrNiMo16-5-1 1.4418
8	NF EN 10088-2-2005
	X4CrNiMo16-5-1 1.4418
9	NF EN 10088-1-2005
	X4CrNiMo16-5-1 1.4418
10	NF EN 10028-7-2008
	X4CrNiMo16-5-1 1.4418
11	NF EN 10028-7-2000
	X4CrNiMo16-5-1 1.4418

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!