Home Material NF EN 10028-7-2000
简体 | 繁體
Grade X6CrNiTiB18-10
1.4941
Corresponding Standard NF EN 10028-7-2000
Flat Products Made of Steels for Pressure Purposes Part 7: Stainless Steels
Classification Austenitic Stainless Steel
Density 7.9 g/cm3
X6CrNiTiB18-10 Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni B More
Minimum Value 0.04 - - - - 17 9 0.0015 Ti:5×C~0.7
Maximum Value 0.08 1 2 0.035 0.015 19 12 0.005
◎ Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.
X6CrNiTiB18-10 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Impact Energy Absorption
KV2
J
C：T ≤ 6 +AT 510~710 Rp0.2：≥220
Rp1.0：≥250
①②		 T ＜ 3mm: ≥40
T ≥ 3mm: ≥ 40
②③		 20℃：
(l: ≥100；t: ≥60)
H：T ≤ 12 +AT 510~710 Rp0.2：≥200
Rp1.0：≥240
①②		 T ＜ 3mm: ≥40
T ≥ 3mm: ≥ 40
②③		 20℃：
(l: ≥100；t: ≥60)
P：T ≤ 75 +AT 490~690 Rp0.2：≥200
Rp1.0：≥240
①②		 T ＜ 3mm: ≥40
T ≥ 3mm: ≥ 40
②③		 20℃：
(l: ≥100；t: ≥60)
◎ C-Cold rolled strip；H-Hot rolled strip；P-Hot rolled plate；T-Thickness；t-transverse；l-Longitudinal
◎ +A=annealed；+AT=solution annealed；+QT = quenched and tempered；+RA=recrystallizing annealed condition
X6CrNiTiB18-10 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X6CrNiTiB 18-10 1.4941
2 EN 10269-2006
X6CrNiTiB18-10 1.4941
3 EN 10302-2008
X6CrNiTiB 18-10 1.4941
4 ISO TS 15510-2003
X6CrNiTiB18-10
5 EN 10269-2013
X6CrNiTiB 18-10 1.4941
6 ISO 15510-2014
X6CrNiTiB18-10 4941-321-09-I
7 NF EN 10269-1999
X6CrNiTiB18-10 1.4941
8 DIN EN 10269-2014
X6CrNiTiB 18-10 1.4941
9 ISO 9328-7-2018
X6CrNiTiB18-10
10 NF EN 10088-1-2005
X6CrNiTiB18-10 1.4941
11 NF EN 10028-7-2008
X6CrNiTiB18-10 1.4941
12 NF EN 10028-7-2000
X6CrNiTiB18-10 1.4941

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!