CuNi18Zn19Pb1 CW408J - EN 12166-1998

Grade	CuNi18Zn19Pb1
European Standard Steel Grade	CW408J
Corresponding Standard	EN 12166-1998
Classification	Copper and Copper Alloys
Density	8.7 g/cm³

CuNi18Zn19Pb1 Chemical Element Composition Content (%)

Component	Fe	Mn	Ni	Cu	Pb	Sn	Other Total	More
Minimum Value	-	-	17	59.5	0.5	-	-	Zn:余量
Maximum Value	0.3	0.7	19	62.5	1.5	0.2	0.2	Zn:余量

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

CuNi18Zn19Pb1 Mechanical Properties

diameter③ d mm	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
1.5≤d≤12	CW408J-R450	1/2 Hard; R450	≥450	≈320*	≥8(A100)； ≥10(A11.3)； ≥12(A)
1.5≤d≤12	CW408J-H120	1/2 Hard; H120				HV: 120~160
1.5≤d≤10	CW408J-R570	Hard; R570	≥570	≈460*	≥2*(A100)； ≥5(A11.3)； ≥8(A)
1.5≤d≤10	CW408J-H150	Hard; H150				HV: 150~200
1.5≤d≤12	CW408J-M	M	No specification	No specification	No specification	No specification

①Material condition designation: H-Hardness (Brinell or Vickers), the suffix number indicates the hardness value; R-Tensile strength, the suffix number indicates the minimum tensile strength; M-As manufactured, without specified mechanical properties
②A100, A11.3, A-gauge length
③Or equivalent cross-sectional area for polygonal wire.

Approximate Comparison Table Cupper and cupper alloy

Germany		European Standard
DIN EN/DIN	W-Nr.	EN	Numerical Grade
CuNi18Zn19Pb1	2.0790	CuNi18Zn19Pb1	CW408J

CuNi18Zn19Pb1 Corresponding Standards(Same grade name, different standards)

1	EN 12166-1998
	CuNi18Zn19Pb1 CW408J
2	EN 12166-2016
	CuNi18Zn19Pb1 CW408J
3	DIN 17672-1-1983
	CuNi18Zn19Pb1 2.0790
4	DIN EN 12166-2016
	CuNi18Zn19Pb1 CW408J
5	DIN EN 12166-1998
	CuNi18Zn19Pb1 CW408J
6	EN 12167-2024
	CuNi18Zn19Pb1 CW408J

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!