Home Material NF EN 10028-7-2000
简体 | 繁體
Grade X2CrNiMoN17-13-3
1.4429
Corresponding Standard NF EN 10028-7-2000
Flat products made of steels for pressure purposes Part 7: Stainless steels
Classification Austenitic Stainless Steel
X2CrNiMoN17-13-3 Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni Mo N
Minimum Value - - - - - 16.5 11 2.5 0.12
Maximum Value 0.03 1 2 0.045 0.015 18.5 14 3 0.22
◎ Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.
X2CrNiMoN17-13-3 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Impact Energy Absorption
KV2
J
C：T ≤ 6 +AT 580~780 Rp0.2：≥300
Rp1.0：≥330
①②		 T ＜ 3mm: ≥35
T ≥ 3mm: ≥ 35
②③		 20℃：
(l: ≥100；t: ≥60)
-196℃：
(t: ≥60)
H：T ≤ 12 +AT 580~780 Rp0.2：≥280
Rp1.0：≥320
①②		 T ＜ 3mm: ≥35
T ≥ 3mm: ≥ 35
②③		 20℃：
(l: ≥100；t: ≥60)
-196℃：
(t: ≥60)
P：T ≤ 75 +AT 580~780 Rp0.2：≥280
Rp1.0：≥320
①②		 T ＜ 3mm: ≥40
T ≥ 3mm: ≥ 40
②③		 20℃：
(l: ≥100；t: ≥60)
-196℃：
(t: ≥60)
Steel: 20℃ ⑤ - ≥580 Rp0.2：≥280
Rp1.0：≥320
≥35 -
Steel: -80℃ ⑤ - ≥800 Rp0.2：≥380
Rp1.0：≥450
≥30 -
Steel: -150℃ ⑤ - ≥1000 Rp0.2：≥500
Rp1.0：≥600
≥30 -
Steel: -196℃ ⑤ - ≥1150 Rp0.2：≥600
Rp1.0：≥700
≥30 -
◎ C-Cold rolled strip；H-Hot rolled strip；P-Hot rolled plate；T-Thickness；t-transverse；l-Longitudinal
◎ +A=annealed；+AT=solution annealed；+QT = quenched and tempered；+RA=recrystallizing annealed condition
X2CrNiMoN17-13-3 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X2CrNiMoN 17-13-3 1.4429
2 EN 10296-2-2005
X2CrNiMoN17-13-3 1.4429
3 EN 10253-4-2003
X2CrNiMoN 17-13-3 1.4429
4 EN 10263-5-2001
X2CrNiMoN17-13-3 1.4429
5 EN 10269-2006
X2CrNiMoN17-13-3 1.4429
6 EN 10250-4-1999
X2CrNiMoN 17-13-3 1.4429
7 EN 10088-2-2005
X2CrNiMoN 17-13-3 1.4429
8 DIN 17440-1972
X2CrNiMoN 17-13-3 X2CrNiMoN 18-13 1.4429
9 EN 10088-3-2005
X2CrNiMoN 17-13-3 1.4429
10 EN 10297(2)-2005
X2CrNiMoN 17-13-3 1.4429
11 EN 10269-2013
X2CrNiMoN 17-13-3 1.4429
12 EN 10088-3-2014
X2CrNiMoN 17-13-3 1.4429
13 NF EN 10269-1999
X2CrNiMoN17-13-3 1.4429
14 DIN EN 10263-5-2018
X2CrNiMoN 17-13-3 1.4429
15 DIN EN 10269-2014
X2CrNiMoN 17-13-3 1.4429
16 ISO 9328-7-2018
X2CrNiMoN17-13-3
17 DIN EN 10088-3-2014
X2CrNiMoN 17-13-3 1.4429
18 ISO 4954-2018
X2CrNiMoN17-13-3 4429-316-53-I
19 NF EN 10088-2-2005
X2CrNiMoN17-13-3 1.4429
20 NF EN 10088-1-2005
X2CrNiMoN17-13-3 1.4429
21 NF EN 10028-7-2008
X2CrNiMoN17-13-3 1.4429
22 NF EN 10296-2-2005
X2CrNiMoN17-13-3 1.4429
23 NF EN 10028-7-2000
X2CrNiMoN17-13-3 1.4429
24 EN 10263-5-2017
X2CrNiMoN 17-13-3 1.4429
25 ISO 4954-2-2024
X2CrNiMoN17-13-3 4429-316-53-I
26 DIN EN 10296-2-2006
X2CrNiMoN17-13-3 1.4429

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!