USA UNS C36000
ASTM
Specification or Grade		 B16
SAE
Steel Number		 CA360
Old Grade
Corresponding Standard SAE J 461-2002
Wrought and Cast Copper Alloys
Classification Copper and Copper Alloys
Density 8.5 g/cm3
Chemical Element Composition Content (%)
Component Cu Pb Zn
Nominal Value 62 3 35
Mechanical Properties
size section
s
mm		 Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Fatigue Limit
Bending σ-1
Mpa 		Elongation or Extension Rate
δ
% 		Reduction of Area
ψ
% 		Hardness
HBW 		Bending Strength σw
Mpa
Bar; s=25 Softening 340 Rp0.5: 125 - 53(L0=50) 58 HRF: 68 Shear Strength: 205
Bar; s=6 1/2 Hard 470 Rp0.5: 360 - 18(L0=50) 48 HRB: 80 Shear strength: 260
Bar; s=25 1/2 Hard 400 Rp0.5: 310 - 25(L0=50) 50 HRB: 78 Shear strength: 235
Bar; s=50 1/2 Hard 380 Rp0.5: 305 140 (Cycle 1 million times)
95 (Cycle 3 million times)		 32(L0=50) 52 HRB: 75 Shear strength: 220
Bars; s=3 Hard 585 Rp0.5: 345 - - - -
Bar; s=6 Hard 515 Rp0.5: 275 - 5(L0=4d) - - -
Bar; s=18 Hard 485 Rp0.5: 240 - 10(L0=4d) - - -
Flat Bar; s=25×150 Softening 330 Rp0.5: 140 - 25(L0=4d) - - Shear Strength: 205
Flat Bar; s>25×150 Softening 310 Rp0.5: 125 - 30(L0=4d) - - Shear strength: 195
Flat Bar; s=6×25 1/2 Hard 385 Rp0.5: 310 - 20(L0=4d) - HRB: 75 Shear strength: 230
Flat Bar; s=12×150 1/2 Hard 345 Rp0.5: 205 - 20(L0=4d) - - Shear Strength: 205
Flat Bar; s=50×50 1/2 Hard 340 Rp0.5: 205 - 25(L0=4d) - - Shear Strength: 205
Flat Bar; s=50×150 1/2 Hard 310 Rp0.5: 170 - 25(L0=4d) - - Shear strength: 185
Flat Material; s＞50×100 1/2 Hard 310 Rp0.5: 170 - 25(L0=4d) Shear strength: 185
Approximate Comparison Table brass
China United States International Organization for Standardization Germany European Standard Russia United Kingdom
GB ISC ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. EN Numerical Grade GOST Commercial Grade BS EN/BS
HPb62-3 C36000 62Cu-35Zn-3Pb C36000 CuZn36Pb3 C36000 CuZn36Pb3 C36000
2.0375 		CuZn36Pb3 CW603N ЛС62-3 CZ124 C36000

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!