06Cr15Ni25Ti2MoAIVB S66286 - Q/YT 102-2019

Grade	06Cr15Ni25Ti2MoAIVB
Other Names
Corresponding Standard	Q/YT 102-2019 Stainless Steel Wire Rods for Cold Heading
Classification	Precipitation-Hardening Stainless Steel

06Cr15Ni25Ti2MoAIVB Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo	Ti	V	B	Al
Minimum Value	-	-	-	-	-	13.5	24	1	1.9	0.1	0.001	-
Maximum Value	0.08	1	2	0.03	0.02	16	27	1.5	2.35	0.5	0.01	0.35

06Cr15Ni25Ti2MoAIVB Mechanical Properties

diameter d mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %
4.5≤d≤10	Post-Rolling Pickled Condition	560~680	≥35	≥50
4.5≤d≤10	Solution Pickled Condition	530~650	≥35	≥55
10≤d≤16	Post-Rolling Pickled Condition	540~640	≥35	≥50
10≤d≤16	Solution Pickled Condition	500~620	≥35	≥55

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!