Grade ML08Al
China ISC U40088
Corresponding Standard GB /T 6478-2015
Steels For Cold Heading And Cold Extruding
Classification Carbon Steel
Properties Forgability
ML08Al Chemical Element Composition Content (%)
Component C Si Mn P S Al a
Minimum Value 0.05 - 0.3 - - 0.02
Maximum Value 0.1 0.1 0.6 0.035 0.035 -
ML08Al Mechanical Properties
Tensile Strength
σb
Mpa 		Reduction of Area
ψ
%
≤470 ≥60
1 Approximate Comparison Table Cold Heading Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France Russia United Kingdom
GB ISC CNS JIS KS ASTM/AISI UNS ISO DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ML08Al U40088 SWRCH8A SWRCH8A SWRCH8A 1010 G10100 CC8X
(A2R) 		QSt34-3
(C7C) 		1.0213 FB8
FR8 		08Ю 0/1
2 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion
China Japan United States International Organization for Standardization European Standard
GB ISC JIS ASTM ISO EN Numerical Grade
ML08Al U40088 SWRCH8A 1008 CC8A C8C 1.0213
ML08Al Corresponding Standards(Same grade name, different standards)
1 GB T 6478-2001
ML08Al U40088
2 GB /T 6478-2015
ML08Al U40088
3 GB /T 28906-2012
ML08Al U40088
4 GB /T 5953.2-2009
ML08Al
5 Q/ASB 234-2018
ML08Al
6 Q/XG 114-2016
ML08Al
7 GB /T 28906-2025
ML08Al U40088

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!