304S11 - BS 970-3-1991

Grade	304S11
Corresponding Standard	BS 970-3-1991 Specification for wrought steel for machanical and allied engineering purposes part 3:bright bars for general engineering purposes
Classification	Austenitic Stainless Steel
Properties	Strength Corrosion Resistance Low-Temperature Toughness Impact Toughness Forgability

304S11 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu ^*	Mo ^*	Ti ^*	Nb ^*
Minimum Value	-	-	-	-	-	17	9	-	-	-	-
Maximum Value	0.03	1	2	0.045	0.03	19	12	0.7	1	0.1	0.2

• For older grades of stainless steel, see Table 2 of standard BS 970-4-1970

304S11 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Bars; d≤19	Cold Drawing	≥865	≥695	≥12
Bars; 19<d≤25	Cold Drawing	≥790	≥555	≥15
Bars; 25<d≤32	Cold Drawing	≥725	≥450	≥20
Bars; 32<d≤38	Cold Drawing	≥695	≥340	≥28
Bars; 38<d≤45	Cold Drawing	≥650	≥310	≥28
Bars; d≤19	Annealing Treatment, Final Cold Drawing	≥600	≥375	≥15
Bars; d>19	Annealing Treatment, Final Cold Drawing	≥550	≥325	≥20
Bars; d<160	Final Softening*	≥480	≥180	≥40

1 Approximate Comparison Table Austenitic Stainless Steel

2 Approximate Comparison Table Austenitic Stainless Steel