1008 G10080 - ASTM A853-2019

Grade	1008
USA UNS	G10080
AISI American Iron and Steel Institute	1008
Corresponding Standard	ASTM A853-2019 Steel Wire, Carbon, for General Use
Classification	Carbon Steel

1008 Mechanical Properties

diameter d mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa
d＜0.89	Intermediate Annealing Annealing	≤655 ≤485
0.89≤d≤1.46	Intermediate annealing Annealing	≤620 ≤450
1.47≤d≤2.17	Cold drawing Intermediate annealing Annealing	≤690 ≤620 ≤450
2.18≤d≤3.27	Cold drawing Intermediate annealing Annealing	≤585 ≤620 ≤450
3.28≤d≤4.5	Cold drawing Intermediate annealing Annealing	≤515 ≤570 ≤450
4.51≤d≤6.35	Cold drawing Intermediate annealing Annealing	≤450 ≤515 ≤450

1 Approximate Comparison Table High-Quality Carbon Structural Steel

2 Approximate Comparison Table High-Quality Carbon Structural Steel

3 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		Japan	United States	International Organization for Standardization	European Standard
GB	ISC	JIS	ASTM	ISO	EN	Numerical Grade
ML08Al	U40088	SWRCH8A	1008	CC8A C8C	C8C	1.0213

4 Approximate Comparison Table High-Quality Carbon Structural Steel

China	Japan	United States	International Organization for Standardization	Germany	France	European Standard		Russia	Sweden	United Kingdom
GB	JIS	SAE	ISO	DIN EN/DIN	NF EN/NF	EN	Numerical Grade	GOST	SS	BS EN/BS
08 08F	SPCC	1008 1010	Cr01 CR22	FeP01 St12	C F12 FeP01	DC01 FeP01	1.0330	08kp 08ps	1142	CR4 FeP01

5 Approximate Comparison Table High-Quality Carbon Structural Steel

China	Japan	United States	International Organization for Standardization	European Standard
GB	JIS	ASTM/AISI	ISO	EN
GB/T 699-2015 08	JIS G4051:2005 JIS G3506:2004 S10C	ASTM A29/A29M:2005 1008	ISO 683-18:1996 C10	EN 10083-1:1991+A1:1996 EN 10084:1998 C10E

1008 Corresponding Standards(Same grade name, different standards)